Corrosion behavior of low alloy steels in a wet–dry acid humid environment
来源期刊：International Journal of Minerals Metallurgy and Materials2016年第9期
论文作者：Qing-he Zhao Wei Liu Jian-wei Yang Yi-chun Zhu Bin-li Zhang Yong Li
文章页码：1076 - 1086
摘 要：The corrosion behavior of corrosion resistant steel（CRS） in a simulated wet–dry acid humid environment was investigated and compared with carbon steel（CS） using corrosion loss, polarization curves, X-ray diffraction（XRD）, scanning electron microscopy（SEM）, electron probe micro-analysis（EPMA）, N2 adsorption, and X-ray photoelectron spectroscopy（XPS）. The results show that the corrosion kinetics of both steels were closely related to the composition and compactness of the rust, and the electrochemical properties of rusted steel. Small amounts of Cu, Cr, and Ni in CRS increased the amount of amorphous phases and decreased the content of γ-Fe OOH in the rust, resulting in higher compactness and electrochemical stability of the CRS rust. The elements Cu, Cr, and Ni were uniformly distributed in the CRS rust and formed CuFeO2, Cu2O, CrOOH, NiFe2O4, and Ni2O3, which enhanced the corrosion resistance of CRS in the wet–dry acid humid environment.
Qing-he Zhao1，Wei Liu1，Jian-wei Yang2，Yi-chun Zhu1，Bin-li Zhang1，Min-xu Lu1
1. Institute for Advanced Materials and Technology, University of Science and Technology Beijing2. Shougang Research Institute of Technology
摘 要：The corrosion behavior of corrosion resistant steel（CRS） in a simulated wet–dry acid humid environment was investigated and compared with carbon steel（CS） using corrosion loss, polarization curves, X-ray diffraction（XRD）, scanning electron microscopy（SEM）, electron probe micro-analysis（EPMA）, N2 adsorption, and X-ray photoelectron spectroscopy（XPS）. The results show that the corrosion kinetics of both steels were closely related to the composition and compactness of the rust, and the electrochemical properties of rusted steel. Small amounts of Cu, Cr, and Ni in CRS increased the amount of amorphous phases and decreased the content of γ-Fe OOH in the rust, resulting in higher compactness and electrochemical stability of the CRS rust. The elements Cu, Cr, and Ni were uniformly distributed in the CRS rust and formed CuFeO2, Cu2O, CrOOH, NiFe2O4, and Ni2O3, which enhanced the corrosion resistance of CRS in the wet–dry acid humid environment.
关键词：