Primary crystallization process of rapidly solidified Al-Ni-Cu-Nd metallic glasses under continuous heating regime

来源期刊：中国有色金属学报(英文版)2003年第4期

论文作者：肖于德 黎文献 D.Jacovkis

文章页码：764 - 768

Key words：rapid solidification; Al-rich amorphous alloy; crystallization; nucleation; grain growth mechanism

Abstract: Rapidly solidified Al₈₇Ni₇Cu₃Nd₃ metallic glasses were prepared by using melt spinning. Its calorimetric behavior was characterized by using differential scanning calorimeter. The metallic glasses were partially crystallized under continuous heating regime. Primary crystallization was studied through structural characterization of the amorphous and partially crystallized ribbons by means of conventional X-ray diffraction and transmission electron microscopy with selected area electron diffraction. The results show that, the as-spun ribbons are fully amorphous and homogeneous on the micron scale, but contain high density of nanoscale quenched-in clusters or crystallite embryos. Primary crystallization mainly leads to formation of two-phase mixture of α-Al nanocrystalline and residual amorphous phase. Precipitation of α-Al nanoparticles is limited by build-up and overlapped diffusion field of solute atoms with low diffusion rate. At the earlier stage of primary crystallization the crystal nuclei exhibit high density and growth rate. With the α-Al crystal growing, the crystal growth rate decreases, and even at the later stage further crystallization into α-Al crystal becomes difficult to occur due to thermal stabilization of the residual nickel and neodymium-enriched amorphous phase, the saturated values of crystallized volume fraction and α-Al crystal diameter getting to 20%-30% and 5-15nm.