SPHERICAL MICROSTRUCTURE FORMATION OF THE SEMI-SOLID HIGH CHROMIUM CAST IRON Cr20Mo2
来源期刊:Acta Metallurgica Sinica2004年第1期
论文作者:W.M.Mao X.Y.Zhong A.M.Zhao
Key words:high chromium cast iron; semi-solid; electromagnetic stirring;
Abstract: The nondendritic semi-solid slurry preparation of high chromium cast iron Cr20Mo2 has been studied in this paper. The experiments show that the proeutectic austenitic particles are more spherical under a larger stirring power condition, even if the stirring time is shorter, while the proeutectic austenitic particles are not very much spherical under a smaller stirring power condition and some proeutectic austenitic dendrites also exist, even if the stirring time is very long. The experiments also show that when stirred for 5 6 minutes under the test condition, the semi-solid slurry with 40vol. %-50vol. % solid fraction and spherical proeutectic austenite in the size of 50-80μm can be obtained.
W.M.Mao1,X.Y.Zhong1,A.M.Zhao1
(1.University of Science & Technology Beijing, Beijing 100083, China)
Abstract:The nondendritic semi-solid slurry preparation of high chromium cast iron Cr20Mo2 has been studied in this paper. The experiments show that the proeutectic austenitic particles are more spherical under a larger stirring power condition, even if the stirring time is shorter, while the proeutectic austenitic particles are not very much spherical under a smaller stirring power condition and some proeutectic austenitic dendrites also exist, even if the stirring time is very long. The experiments also show that when stirred for 5 6 minutes under the test condition, the semi-solid slurry with 40vol. %-50vol. % solid fraction and spherical proeutectic austenite in the size of 50-80μm can be obtained.
Key words:high chromium cast iron; semi-solid; electromagnetic stirring;