Spheroidizing Behavior and Spheroidizing Kinetics of W-phase During Solid-Solution Treatment in Mg–Zn–Y–Mn–(B) Alloys
来源期刊:Acta Metallurgica Sinica2017年第5期
论文作者:Kai Yang Jin-Shan Zhang Xi-Mei Zong Wei Liu Chun-Xiang Xu
文章页码:464 - 469
摘 要:The spheroidizing mechanism of W-phase in the Mg–Zn–Y–Mn–(B) alloys during solid-solution treatment was investigated by using kinetic methodologies. The microstructure and mechanical properties of heat-treated Mg94Zn2.5-Y2.5Mn1 alloy containing 0.003 wt% B were compared with heat-treated Mg94Zn2.5-Y2.5Mn1 alloy. The heat-treated Mg94Zn2.5-Y2.5Mn1 alloy with 0.003 wt% B contained fine and uniform W-phase particles, which exhibited optimal mechanical performance. The ultimate tensile strength, yield strength and elongation were 287.7, 125.5 MPa and 21.1%,respectively.
Kai Yang1,2,Jin-Shan Zhang1,2,Xi-Mei Zong1,2,Wei Liu1,2,Chun-Xiang Xu1,2
1. College of Materials Science and Engineering, Taiyuan University of Technology2. Shanxi Key Laboratory of Advanced Magnesium-based Materials
摘 要:The spheroidizing mechanism of W-phase in the Mg–Zn–Y–Mn–(B) alloys during solid-solution treatment was investigated by using kinetic methodologies. The microstructure and mechanical properties of heat-treated Mg94Zn2.5-Y2.5Mn1 alloy containing 0.003 wt% B were compared with heat-treated Mg94Zn2.5-Y2.5Mn1 alloy. The heat-treated Mg94Zn2.5-Y2.5Mn1 alloy with 0.003 wt% B contained fine and uniform W-phase particles, which exhibited optimal mechanical performance. The ultimate tensile strength, yield strength and elongation were 287.7, 125.5 MPa and 21.1%,respectively.
关键词: