Friction and Wear Property of Cu-Cr Alloy

来源期刊:JOURNAL OF RARE EARTHS2007年增刊第1期

论文作者:Liu Jianhua Zhang Ruijun Gao Hong Wang Yuhui

Key words:Cu-Cr alloy; friction and wear; loads and speed; rare earths;

Abstract: The friction and wear behaviors of the Cu-Cr alloy sliding against GCr15 steel at different loads and rotate speed conditions were evaluated, and the worn surface morphologies were observed on a scanning electron microscope. Results show that as loads and rotate speed increase, the wear loss weight increases, by comparison, the biggest friction coefficient of Cu-Cr alloy was obtained at load 100N and rotate speed at 100 r·min-1 friction condition. Moreover, the dominant wear forms was plough wear.

详情信息展示

Friction and Wear Property of Cu-Cr Alloy

Liu Jianhua1,Zhang Ruijun1,Gao Hong1,Wang Yuhui1

(1.State Key laboratory of Metastable Materials Science and Technology, Yan Shan University, Qinhuangdao 066004, China)

Abstract:The friction and wear behaviors of the Cu-Cr alloy sliding against GCr15 steel at different loads and rotate speed conditions were evaluated, and the worn surface morphologies were observed on a scanning electron microscope. Results show that as loads and rotate speed increase, the wear loss weight increases, by comparison, the biggest friction coefficient of Cu-Cr alloy was obtained at load 100N and rotate speed at 100 r·min-1 friction condition. Moreover, the dominant wear forms was plough wear.

Key words:Cu-Cr alloy; friction and wear; loads and speed; rare earths;

【全文内容正在添加中】

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号