Effect of cold rolling and first precipitates on the coarsening behavior of γ″-phases in Inconel 718 alloy
来源期刊:International Journal of Minerals Metallurgy and Materials2016年第9期
论文作者:Jing-ling Zhang Qian-ying Guo Yong-chang Liu Chong Li Li-ming Yu Hui-jun Li
文章页码:1087 - 1096
摘 要:The coarsening behaviors of γ″-phase particles in Inconel 718 alloy aged at 750, 800, and 850℃ were investigated by scanning electron microscopy(SEM). Detailed observations and quantitative measurements were conducted to characterize the coarsening behavior of the γ″-phase under various aging conditions. The experimental results indicate that the existence of the δ-phase retards the formation and coarsening of the γ″-phase, without influencing its final particle size or amount. Moreover, when cold rolled with a reduction of 50%, the dimensions of the γ″ particles in Inconel 718 alloy decrease with increasing aging time. Furthermore, the coarsening behavior of the γ″-phase in the Inconel 718 alloy after a normal aging treatment(sample A) and that of the primary δ-phase(sample B) follow the Lifshitz–Slyozov–Wagner(LSW) diffusion-controlled growth theory; the thus-obtained activation energies for the γ″-phase are 292 k J·mol-1and 302 k J·mol-1, respectively.
Jing-ling Zhang,Qian-ying Guo,Yong-chang Liu,Chong Li,Li-ming Yu,Hui-jun Li
State Key Lab of Hydraulic Engineering Simulation and Safety, School of Materials Science & Engineering, Tianjin University
摘 要:The coarsening behaviors of γ″-phase particles in Inconel 718 alloy aged at 750, 800, and 850℃ were investigated by scanning electron microscopy(SEM). Detailed observations and quantitative measurements were conducted to characterize the coarsening behavior of the γ″-phase under various aging conditions. The experimental results indicate that the existence of the δ-phase retards the formation and coarsening of the γ″-phase, without influencing its final particle size or amount. Moreover, when cold rolled with a reduction of 50%, the dimensions of the γ″ particles in Inconel 718 alloy decrease with increasing aging time. Furthermore, the coarsening behavior of the γ″-phase in the Inconel 718 alloy after a normal aging treatment(sample A) and that of the primary δ-phase(sample B) follow the Lifshitz–Slyozov–Wagner(LSW) diffusion-controlled growth theory; the thus-obtained activation energies for the γ″-phase are 292 k J·mol-1and 302 k J·mol-1, respectively.