Luminescence properties of Eu2+ -doped Ba3Si6O12N2 green phosphor: concentration quenching and thermal stability
来源期刊：JOURNAL OF RARE EARTHS2013年第2期
论文作者：陈观通 庄卫东 胡运生 刘元红 刘荣辉 何华强
文章页码：113 - 118
摘 要：The efficient Eu2+ -doped Ba3 Si6O12N2 green phosphors were prepared by a traditional solid state reaction method under N2 /H2 atmosphere at a temperature up to 1350 oC for 12h. Photoluminescence （PL） properties showed a broad emission band with a peak of 525 nm and the full width of half-emission maximums （FWHM） of 70 nm under 460 nm light irradiation. The X-ray diffraction patterns （XRD） and scanning electron microscope （SEM） images of the synthesized powder demonstrated its pure phase and excellent crystallization. Quenching concentration in this phosphor was found to be 0.3. The mechanisms of concentration quenching and redshift of emission peak with increasing concentration of Eu2+ were studied. The temperature dependence measurement of this green phosphor revealed excellent thermal quenching property compared to silicate green phosphor. It is believed that Ba3 Si6O12N2 :Eu2+ is an excellent green phosphor for UV or blue chip based white LEDs.
陈观通，庄卫东，胡运生，刘元红，刘荣辉，何华强
National Engineering Research Center for Rare Earth Materials,General Research Institute for Nonferrous Metals,and Grirem Advanced Materials Co.,Ltd.
摘 要：The efficient Eu2+ -doped Ba3 Si6O12N2 green phosphors were prepared by a traditional solid state reaction method under N2 /H2 atmosphere at a temperature up to 1350 oC for 12h. Photoluminescence （PL） properties showed a broad emission band with a peak of 525 nm and the full width of half-emission maximums （FWHM） of 70 nm under 460 nm light irradiation. The X-ray diffraction patterns （XRD） and scanning electron microscope （SEM） images of the synthesized powder demonstrated its pure phase and excellent crystallization. Quenching concentration in this phosphor was found to be 0.3. The mechanisms of concentration quenching and redshift of emission peak with increasing concentration of Eu2+ were studied. The temperature dependence measurement of this green phosphor revealed excellent thermal quenching property compared to silicate green phosphor. It is believed that Ba3 Si6O12N2 :Eu2+ is an excellent green phosphor for UV or blue chip based white LEDs.
关键词：