Superplasticity in magnesium-based composite

来源期刊:中国有色金属学报(英文版)2003年第z1期

论文作者:ZHAO Min(赵 敏) WU Kun(吴 昆) YAN Feng(严 峰) YANG De-zhuang(杨德庄)

文章页码:195 - 197

Key words:SiC whiskers; magnesium matrix composite; superplasticity; activation energy; texture

Abstract: Superplasticity in a SiCw/ZK60 composite was studied. The samples were tested at temperatures ranging from 573K to 723K and at the initial strain rates ranging from 8.3×10-4s-1 to 8.3×10-2s-1. A maximum elongation of 200% was obtained at 613K and 1.67×10-2s-1 with a m-value of 0.35. The activation energy (98kJ/mol) approximates that for grain boundary diffusion (92kJ/mol) in magnesium. A strong 〈111〉 fibre texture was developed in SiC whiskers during superplastic deformation.

详情信息展示

Superplasticity in magnesium-based composite

ZHAO Min(赵 敏), WU Kun(吴 昆), YAN Feng(严 峰), YANG De-zhuang(杨德庄)

(School of Materials Science and Engineering,
Harbin Institute of Technology, Harbin 150001, China)

Abstract:Superplasticity in a SiCw/ZK60 composite was studied. The samples were tested at temperatures ranging from 573K to 723K and at the initial strain rates ranging from 8.3×10-4s-1 to 8.3×10-2s-1. A maximum elongation of 200% was obtained at 613K and 1.67×10-2s-1 with a m-value of 0.35. The activation energy (98kJ/mol) approximates that for grain boundary diffusion (92kJ/mol) in magnesium. A strong 〈111〉 fibre texture was developed in SiC whiskers during superplastic deformation.

Key words:SiC whiskers; magnesium matrix composite; superplasticity; activation energy; texture

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号