Effects of the precursor size on the morphologies and properties of γ-Ce2S3 as a pigment

来源期刊:Journal of Rare Earths2014年第6期

论文作者:于世泳 王东日 高小龙 苏海全

文章页码:540 - 544

摘    要:Ceria spheres with different sizes and sulfurized products with corresponding morphology were prepared by hydrothermal and gas-solid reaction method at 600–800 °C under CS2 atmosphere for a short time, respectively. Dimensional effect in preparation of γ-Ce2S3 was firstly investigated by means of techniques such as scanning electron microscopy(SEM), X-ray diffraction(XRD), thermal gravimetric analysis(TGA) and spectrophotometer. The results showed that when ceria nanoparticles with small size were used as precursors, the γ-Ce2S3 could be prepared at the lower temperature and the badly sintered products were obtained; when ceria nanoparticles with large size were employed as precursors, pure γ-Ce2S3 was difficultly obtained even if the temperature was up to 800 °C and the products tended to keep their original size. The heat-resistance property of the γ-Ce2S3 with large size was better than the smaller one, and the pure γ-Ce2S3 prepared from precursor with small size had a good pigmentary performance.

详情信息展示

Effects of the precursor size on the morphologies and properties of γ-Ce2S3 as a pigment

于世泳,王东日,高小龙,苏海全

Inner Mongolia Key Laboratory of Chemistry and Physics of Rare Earth Materials School of Chemistry and Chemical Engineering Inner Mongolia University

摘 要:Ceria spheres with different sizes and sulfurized products with corresponding morphology were prepared by hydrothermal and gas-solid reaction method at 600–800 °C under CS2 atmosphere for a short time, respectively. Dimensional effect in preparation of γ-Ce2S3 was firstly investigated by means of techniques such as scanning electron microscopy(SEM), X-ray diffraction(XRD), thermal gravimetric analysis(TGA) and spectrophotometer. The results showed that when ceria nanoparticles with small size were used as precursors, the γ-Ce2S3 could be prepared at the lower temperature and the badly sintered products were obtained; when ceria nanoparticles with large size were employed as precursors, pure γ-Ce2S3 was difficultly obtained even if the temperature was up to 800 °C and the products tended to keep their original size. The heat-resistance property of the γ-Ce2S3 with large size was better than the smaller one, and the pure γ-Ce2S3 prepared from precursor with small size had a good pigmentary performance.

关键词:

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号