中碳钢板坯保护渣性能优化及提高拉速工业试验研究
来源期刊：钢铁2009年第3期
论文作者：赵紫锋 王新华 张炯明 梅峰 康建国
文章页码：24 - 27
关键词：中碳钢； 板坯； 拉速； 保护渣
Key words：medium carbon steel； slab； casting speed； flux
摘 要：通过提高保护渣碱度以及渣中CaF2和Li2O含量,对中碳钢板坯用保护渣进行了优化,并采用优化的保护渣进行了提高拉速工业试验。结果表明:优化的保护渣具有较高结晶温度、较低的粘度和熔点;试验过程中,采用优化的保护渣液渣层厚度平均增加约2 mm,单耗增加0.03 kg/m2;采用优化的保护渣在1.5 m/min拉速下和采用原渣在1.3 m/min拉速下浇铸时,结晶器传热强度、传热的稳定性以及浇铸出的铸坯质量等项目水平相当。
Abstract: By increasing basicity and contents of CaF2 and Li2O,the mold flux for medium carbon steel slab casting was optimized.The optimized flux was adopted in plant trial of increasing casting-speed.The results showed that optimized flux has higher crystallization temperature,lower viscosity and melting point.In plant trial,liquid optimized flux thickness increased by 2 mm approximately,slag consumption increased by 0.03 kg/m2.At a casting speed of 1.3 m/min,heat-transfer intensity,stability and slab quality cast with traditional flux were almost the same as cast with optimized flux at a casting speed of 1.5 m/min.
赵紫锋1，王新华1，张炯明1，梅峰2，康建国2
(1.北京市北京科技大学 冶金与生态工程学院
2.宝山钢铁股份有限公司 技术中心，上海 201900)
摘 要：通过提高保护渣碱度以及渣中CaF2和Li2O含量,对中碳钢板坯用保护渣进行了优化,并采用优化的保护渣进行了提高拉速工业试验。结果表明:优化的保护渣具有较高结晶温度、较低的粘度和熔点;试验过程中,采用优化的保护渣液渣层厚度平均增加约2 mm,单耗增加0.03 kg/m2;采用优化的保护渣在1.5 m/min拉速下和采用原渣在1.3 m/min拉速下浇铸时,结晶器传热强度、传热的稳定性以及浇铸出的铸坯质量等项目水平相当。
关键词：中碳钢； 板坯； 拉速； 保护渣