Fabrication and Thermal Insulating Properties of ITO/PVB Nanocomposites for Energy Saving Glass
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2017年第1期
论文作者：严微 XIAO Haiyan JIANG Tao LI Weibo 张刚申
文章页码：63 - 66
摘 要：Chemical co-precipitation method was used to synthesize tin-doped indium oxide（ITO）nanoparticles,and the subsequent solution co-blend was employed to fabricate ITO/PVB nanocomposites.UV（Ultra-violet）-Vis（Visible）-NIR（Near Infrared） spectra show that the addition of ITO nano particles can significantly enhance the thermal insulating efficiency of ITO/PVB nanocomposites.With increasing ITO content,the thermal insulating efficiency is increased.UV is almost fully absorbed by all ITO/PVB nanocomposites.Vis transmittance-haze spectra reveal that ITO/PVB nanocomposites exhibit higher Vis transmittance over 71.3%and lower haze below 2%when ITO content is in the range of 0.1 wt%-0.7 wt%.The UV-Vis-NIR spectroscopy shows that,under the premise of over 70%transmittance to the visible light,the screening effect of the NIR can be enhanced by 80%with 0.7%ITO/PVB nanocomposite membrane compared with the undoped PVB.The thermal insulating tests indicate that,in comparison with the pure PVB film,nanocomposite films with 0.1 wt%-0.9 wt%ITO can reduce temperature by 3-8 ℃.The results show that this novel nanocomposite can be used for energy-saving glass.
严微1，XIAO Haiyan2，JIANG Tao1，LI Weibo1，张刚申1
1. Hubei Collaborative Innovation Center for Advanced Organic Chemical Materials, Ministry of Education, Key Laboratory of Green Preparation and Application for Functional Materials, Hubei Key Laboratory of Polymer Materials, School of Materials Science & Engineering, Hubei University2. State Key Laboratory of Silicate Materials for Architectures (Wuhan University of Technology)
摘 要：Chemical co-precipitation method was used to synthesize tin-doped indium oxide（ITO）nanoparticles,and the subsequent solution co-blend was employed to fabricate ITO/PVB nanocomposites.UV（Ultra-violet）-Vis（Visible）-NIR（Near Infrared） spectra show that the addition of ITO nano particles can significantly enhance the thermal insulating efficiency of ITO/PVB nanocomposites.With increasing ITO content,the thermal insulating efficiency is increased.UV is almost fully absorbed by all ITO/PVB nanocomposites.Vis transmittance-haze spectra reveal that ITO/PVB nanocomposites exhibit higher Vis transmittance over 71.3%and lower haze below 2%when ITO content is in the range of 0.1 wt%-0.7 wt%.The UV-Vis-NIR spectroscopy shows that,under the premise of over 70%transmittance to the visible light,the screening effect of the NIR can be enhanced by 80%with 0.7%ITO/PVB nanocomposite membrane compared with the undoped PVB.The thermal insulating tests indicate that,in comparison with the pure PVB film,nanocomposite films with 0.1 wt%-0.9 wt%ITO can reduce temperature by 3-8 ℃.The results show that this novel nanocomposite can be used for energy-saving glass.
关键词：