Study on the preparation process of large particle cerium oxide
来源期刊：Journal of Rare Earths2010年第S1期
论文作者：马莹 王宝荣 李莉娜 乔军 苏允兰 王笃金 王晶晶
文章页码：136 - 138
摘 要：The large particle cerium oxide was prepared using oxalic acid as precipitation agent. The effects of preparation conditions on the particle size of cerium oxide were discussed. The results showed that the particle size of cerium oxide could be controlled effectively by the temperature,acidity of the solution,aging time,etc. The optimized preparation process of large particle cerium oxide was obtained. The cerium oxide with size between 50 μm to 150 μm was prepared by the process. Moreover,the cerium oxide particles were dispersed uniformly.
马莹1,2，王宝荣1，李莉娜3，乔军1,2，苏允兰3，王笃金3，王晶晶1,2
1. National Engineering Research Center of Rare Earth Metallurgy and Functional Materials2. Baotou Research Institute of Rare Earths3. Institute of Chemistry,Chinese Academy of Sciences
摘 要：The large particle cerium oxide was prepared using oxalic acid as precipitation agent. The effects of preparation conditions on the particle size of cerium oxide were discussed. The results showed that the particle size of cerium oxide could be controlled effectively by the temperature,acidity of the solution,aging time,etc. The optimized preparation process of large particle cerium oxide was obtained. The cerium oxide with size between 50 μm to 150 μm was prepared by the process. Moreover,the cerium oxide particles were dispersed uniformly.
关键词：