Controlled synthesis and formation mechanism of sodium yttrium fluoride nanotube arrays
来源期刊：Journal of Rare Earths2012年第12期
论文作者：田俐 谭丽 孙起亮 向绍斌 肖秋国 汤建庭 朱广山
文章页码：1260 - 1264
摘 要：Cubic and hexagonal sodium yttrium fluoride were successfully synthesized from yttrium nitrate, sodium fluoride and poly-ethanediol in propanetriol solvent under a facile hydrothermal route. By regulating the molar ratio of yttrium and fluoride, hydrothermal tem-perature and reaction time, the phase and shape of sodium yttrium fluoride were commendably controlled. The as-prepared products were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive X-ray spectrum （EDS） techniques. It was revealed that the hollow-structured Na（Y1.5Na0.5）F6 nanotubes self-assembled and arrayed orientedly to be bamboo raft-shaped. The for-mation of hexagonal Na（Y1.5Na0.5）F6 nanotube arrays was attributed to solid-liquid-solid process and Oswald ripening. This study provided a simple method to prepare hexagonal bamboo raft-shaped Na（Y1.5Na0.5）F6 on a large scale, which broadened their practical applications.
田俐1,2，谭丽1，孙起亮1，向绍斌1，肖秋国1，汤建庭1，朱广山2
1. School of Chemistry and Chemical Engineering,Hunan University of Science and Technology2. State Key Laboratory of Inorganic Synthesis and Preparative Chemistry,College of Chemistry,Jilin University
摘 要：Cubic and hexagonal sodium yttrium fluoride were successfully synthesized from yttrium nitrate, sodium fluoride and poly-ethanediol in propanetriol solvent under a facile hydrothermal route. By regulating the molar ratio of yttrium and fluoride, hydrothermal tem-perature and reaction time, the phase and shape of sodium yttrium fluoride were commendably controlled. The as-prepared products were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive X-ray spectrum （EDS） techniques. It was revealed that the hollow-structured Na（Y1.5Na0.5）F6 nanotubes self-assembled and arrayed orientedly to be bamboo raft-shaped. The for-mation of hexagonal Na（Y1.5Na0.5）F6 nanotube arrays was attributed to solid-liquid-solid process and Oswald ripening. This study provided a simple method to prepare hexagonal bamboo raft-shaped Na（Y1.5Na0.5）F6 on a large scale, which broadened their practical applications.
关键词：