Activity of Reducing Steel Slag of EAF
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2011年第1期
论文作者:郭金祥
文章页码:165 - 171
摘 要:Reducing steel slag (RSS) was mainly acquired from five electric-arc furnace (EAF) steelmaking plants (among them, the products of two plants were carbon steel and those of other plants were stainless steel) for research tests. The chemical properties, compound compositions, activities and contents of main expansive compounds were tested. The results showed that the field sampled RSS had a very high crystallinity and hydraulicity with main chemical compositions close to those of Portland cement. It can be known from the study that in case of C/S ratio higher than 2.0, the main compound compositions are C2S, C3S, C2F and f-CaO. However, after the RSS was stored for six months, an obvious variation occurred with potential pre-hydration in RSS, where the SO3 content was slightly reduced and the compressive activity index was obviously higher than that at the 28th day.
郭金祥
Department of Construction Engineering, National Taiwan University of Science and Technology
摘 要:Reducing steel slag (RSS) was mainly acquired from five electric-arc furnace (EAF) steelmaking plants (among them, the products of two plants were carbon steel and those of other plants were stainless steel) for research tests. The chemical properties, compound compositions, activities and contents of main expansive compounds were tested. The results showed that the field sampled RSS had a very high crystallinity and hydraulicity with main chemical compositions close to those of Portland cement. It can be known from the study that in case of C/S ratio higher than 2.0, the main compound compositions are C2S, C3S, C2F and f-CaO. However, after the RSS was stored for six months, an obvious variation occurred with potential pre-hydration in RSS, where the SO3 content was slightly reduced and the compressive activity index was obviously higher than that at the 28th day.
关键词: