Manufacturing Microporous Foam Zinc Materials with High Porosity By Electrodeposition
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2011年第5期
论文作者：田庆华
文章页码：843 - 846
摘 要：In order to get foam zinc materials of porous metal electrode,a novel method for preparing foam zinc was proposed,in which the polyurethane foam with diameter of 0.3 mm as substrate was processed by degreasing,roughening,activating,electroless plating and electrodeposition.The main factors affecting the process,such as ZnSO4 content,temperature,pH value,current density,and electrodes distance,were investigated comprehensively.The optimal process conditions are 250 g/L ZnSO4,20 g/L Al2（SO4）3,40 g/L KAl（SO4）2,30 g/L Na2SO4,pH=3.5,4.0 cm of electrodes distance and 0.04 A/cm2 current density at 30 ℃.The result shows that adding ultrasonic on the process can elevate the deepening plating ability and current efficiency.Foam zinc material with a high porosity of 92.2% and a three-dimensional network structure can be fabricated by electrodeposition.
田庆华
摘 要：In order to get foam zinc materials of porous metal electrode,a novel method for preparing foam zinc was proposed,in which the polyurethane foam with diameter of 0.3 mm as substrate was processed by degreasing,roughening,activating,electroless plating and electrodeposition.The main factors affecting the process,such as ZnSO4 content,temperature,pH value,current density,and electrodes distance,were investigated comprehensively.The optimal process conditions are 250 g/L ZnSO4,20 g/L Al2（SO4）3,40 g/L KAl（SO4）2,30 g/L Na2SO4,pH=3.5,4.0 cm of electrodes distance and 0.04 A/cm2 current density at 30 ℃.The result shows that adding ultrasonic on the process can elevate the deepening plating ability and current efficiency.Foam zinc material with a high porosity of 92.2% and a three-dimensional network structure can be fabricated by electrodeposition.
关键词：