Hot deformation behavior and processing map of Mg-2Zn-1Al-0.2RE alloy
来源期刊:Journal of Rare Earths2020年第6期
论文作者:Yanxia Niu Jian Hou Fangkun Ning Xingrui Chen Yonghui Jia Qichi Le
文章页码:665 - 675
摘 要:In this study,uniaxial hot compression tests were carried out between 200 and 400℃ over strain rates of0.001-1 s-1 to investigate the hot deformation behavior of Mg-2 Zn-1 Al-0.2 RE alloy with coarse grains.The average activation energy was measured to be 174.51 kJ/mol.In addition,a constitutive relation based on the Arrhenius equation was established.Dynamic recrystallization(DRX) kinetics were studied by Avrami equation to characterize the evolution of DRX volume fraction.DRX was favored at high temperatures of 300-400℃ and low strain rates of 0.001-0.01 s-1.According to dynamic material model and Prasad’s instability criterion,a maximum power dissipation of 38% and 32% occurs at 400℃/0.001 s-1 and 400℃/0.01 s-1,respectively.According to the proce ssing map,330-400℃/0.001-0.01 s-1was determined as the optimum deformation parameter range.
Yanxia Niu,Jian Hou,Fangkun Ning,Xingrui Chen,Yonghui Jia,Qichi Le
Key Laboratory of Electromagnetic Processing of Materials,Ministry of Education,Northeastern University
摘 要:In this study,uniaxial hot compression tests were carried out between 200 and 400℃ over strain rates of0.001-1 s-1 to investigate the hot deformation behavior of Mg-2 Zn-1 Al-0.2 RE alloy with coarse grains.The average activation energy was measured to be 174.51 kJ/mol.In addition,a constitutive relation based on the Arrhenius equation was established.Dynamic recrystallization(DRX) kinetics were studied by Avrami equation to characterize the evolution of DRX volume fraction.DRX was favored at high temperatures of 300-400℃ and low strain rates of 0.001-0.01 s-1.According to dynamic material model and Prasad’s instability criterion,a maximum power dissipation of 38% and 32% occurs at 400℃/0.001 s-1 and 400℃/0.01 s-1,respectively.According to the proce ssing map,330-400℃/0.001-0.01 s-1was determined as the optimum deformation parameter range.
关键词: