Powder injection molding of pure titanium
来源期刊：Rare Metals2009年第3期
论文作者：GUO Shiboa, b, DUAN Bohuab, HE Xinbob, and QU Xuanhuib a Advanced Materials Synthesis and Applied Technology Laboratory, College of Electromechanical Engineering, Hunan University of Science and Engineering, Xiangtan , China b School of Materials Science and Engineering, University of Science and Technology of Beijing, Beijing , China
文章页码：261 - 265
摘 要：An improved wax-based binder was developed for powder injection molding of pure titanium. A critical powder loading of 69 vol.% and a pseudo-plastic flow behavior were obtained by the feedstock based on the binder. The injection molding, debinding, and sintering process were studied. An ideal control of carbon and oxygen contents was achieved by thermal debinding in vacuum atmosphere （10-3 Pa）. The mechanical properties of as-sintered specimens were less than those of titanium made by the conventional press-sintering process. Good shape retention and ±0.04 mm dimension deviation were achieved.
GUO Shiboa, b, DUAN Bohuab, HE Xinbob, and QU Xuanhuib a Advanced Materials Synthesis and Applied Technology Laboratory, College of Electromechanical Engineering, Hunan University of Science and Engineering, Xiangtan 411201, China b School of Materials Science and Engineering, University of Science and Technology of Beijing, Beijing 100083, China
摘 要：An improved wax-based binder was developed for powder injection molding of pure titanium. A critical powder loading of 69 vol.% and a pseudo-plastic flow behavior were obtained by the feedstock based on the binder. The injection molding, debinding, and sintering process were studied. An ideal control of carbon and oxygen contents was achieved by thermal debinding in vacuum atmosphere （10-3 Pa）. The mechanical properties of as-sintered specimens were less than those of titanium made by the conventional press-sintering process. Good shape retention and ±0.04 mm dimension deviation were achieved.
关键词：