Investigation on the 773 K isothermal section of La-Fe-Sn ternary systems by X-ray powder diffraction
来源期刊:Rare Metals2010年第6期
论文作者:CHEN Xianga,b,ZHUANG Yinghonga,and CHEN Yunguic a Key Laboratory of Nonferrous Metal and New Processing Technology of Materials(Ministry of Education of China),Guangxi University,Nanning ,China b Department of Physics and Electronic Information Engineering,Neijiang Teachers College,Neijiang ,China c Department of Metallic Materials Engineering,Sichuan University,Chengdu ,China
文章页码:567 - 571
摘 要:The 773 K isothermal section of the La-Fe-Sn ternary system was investigated and constructed by X-ray powder diffraction(XRD).The existence of two reported ternary intermetallic compounds,La6Fe13Sn and La3FeSn6,is confirmed in this work.Compared with other R-Fe-Sn phase diagrams(R = Pr and Sm),the binary alloys Fe3Sn and Fe5Sn3 are not present.The compound Fe3Sn2 was observed from the XRD pattern of Fe3Sn2 samples,but it is not an equilibrium phase at 773 K and decomposes into Fe and FeSn phases completely for a longer heat treated time.Up to now,the crystal structure data of La2Sn3 has not been reported,so the X-ray pattern of La2Sn3 was only estimated.The phase relationship for this compound was drawn by a dotted line.
摘要:The 773 K isothermal section of the La-Fe-Sn ternary system was investigated and constructed by X-ray powder diffraction(XRD).The existence of two reported ternary intermetallic compounds,La6Fe13Sn and La3FeSn6,is confirmed in this work.Compared with other R-Fe-Sn phase diagrams(R = Pr and Sm),the binary alloys Fe3Sn and Fe5Sn3 are not present.The compound Fe3Sn2 was observed from the XRD pattern of Fe3Sn2 samples,but it is not an equilibrium phase at 773 K and decomposes into Fe and FeSn phases completely for a longer heat treated time.Up to now,the crystal structure data of La2Sn3 has not been reported,so the X-ray pattern of La2Sn3 was only estimated.The phase relationship for this compound was drawn by a dotted line.
关键词: