Bonding Efficacy of a Self-adhesive Resin Cement to Enamel and Dentin
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2014年第6期
论文作者:王林虎 XU Haixing LI Songyang 施斌 LI Rong YE Mingfu YANG Jing
文章页码:1307 - 1312
摘 要:With the objective to evaluate the bonding efficacy of a new self-adhesive resin cement(RelyX Unicem, 3M ESPE) to enamel and dentin using a shear bonding strengths test with or without acid etching pretreatment, flat buccal dentin surface and mesial/distal enamel surface were made using a high-speed diamond bur. Copper rings were luted using Rely X Unicem(RU; 3M ESPE), Panavia F(PF; Kuraray) or Vitique(VI; DMG). For RU, the shear bonding strengths using GL(Gluma Etch, Heraeus) acid etching pretreatment were also tested. The teeth were placed into copper rings(inner diameter: 16 mm, height: 4mm) and embedded in methylmethacrylate resin. The specimens were stored for 24 h in distilled water at 37 ℃ prior to shear bonding strengths testing. In addition, bond failures were examined by optical microscope and categorized as 4 models such as different adhesive, cohesive, or mixed. Shear bonding strengths were calculated by dividing the maximum debonding force over the cross sectional area of each specimen. The Kruskal-Wallis test was used to determine pairwise statistical differences(P < 0.05) in SBS between the experimental groups. For dentin bonding strength, statistical analysis showed that there was no significant difference among RU(12.84 MPa), PF(14.93 MPa) and VI(11.03 MP); and the bonding strengths of them were higher than RU with acid etching pretreatment(9.12 MP). When bonded to enamel, PF(17.99 MP) and VI(17.58 MP) scored significantly higher than RU efficacy.The use of self-adhesive cement Rely X Unicem can obtain the bonding strengths to dentin similar to traditional resin cements. Phosphoric acid etching can improve the bonding strengths of the selfadhesive resin cement to enamel, but was negative for dentin.
王林虎1,XU Haixing2,LI Songyang3,施斌1,LI Rong1,YE Mingfu1,YANG Jing1
1. Department of Implantology, Hospital of Stomatology, Wuhan University2. Department of Pharmaceutical Engineering, School of Chemistry, Chemical Engineering and Life Sciences, Wuhan University of Technology3. Department of Biology, Hongkong Baptist University
摘 要:With the objective to evaluate the bonding efficacy of a new self-adhesive resin cement(RelyX Unicem, 3M ESPE) to enamel and dentin using a shear bonding strengths test with or without acid etching pretreatment, flat buccal dentin surface and mesial/distal enamel surface were made using a high-speed diamond bur. Copper rings were luted using Rely X Unicem(RU; 3M ESPE), Panavia F(PF; Kuraray) or Vitique(VI; DMG). For RU, the shear bonding strengths using GL(Gluma Etch, Heraeus) acid etching pretreatment were also tested. The teeth were placed into copper rings(inner diameter: 16 mm, height: 4mm) and embedded in methylmethacrylate resin. The specimens were stored for 24 h in distilled water at 37 ℃ prior to shear bonding strengths testing. In addition, bond failures were examined by optical microscope and categorized as 4 models such as different adhesive, cohesive, or mixed. Shear bonding strengths were calculated by dividing the maximum debonding force over the cross sectional area of each specimen. The Kruskal-Wallis test was used to determine pairwise statistical differences(P < 0.05) in SBS between the experimental groups. For dentin bonding strength, statistical analysis showed that there was no significant difference among RU(12.84 MPa), PF(14.93 MPa) and VI(11.03 MP); and the bonding strengths of them were higher than RU with acid etching pretreatment(9.12 MP). When bonded to enamel, PF(17.99 MP) and VI(17.58 MP) scored significantly higher than RU efficacy.The use of self-adhesive cement Rely X Unicem can obtain the bonding strengths to dentin similar to traditional resin cements. Phosphoric acid etching can improve the bonding strengths of the selfadhesive resin cement to enamel, but was negative for dentin.
关键词: