Microstructure and Mechanical Properties of C/C-ZrC-SiC Composites Fabricated by Reactive Melt Infiltration with Zr,Si Mixed Powders
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2013年第8期
论文作者：Xin Yang Zhean Su Qizhong Huang Xiao Fang Liyuan Chai
文章页码：702 - 710
摘 要：<正>To meet the increasing demand for advanced materials capable of operation over 2000℃for future thermal protection systems application,C/C—ZrC—SiC composites were fabricated by reactive melt infiltration（RMI） with Zr,Si mixed powders as raw materials.The structural evolution and formation mechanism of the C/C—ZrC -SiC composites were discussed,and the mechanical property of the as-prepared material was investigated by compression test.The results showed that after the RMI process,a special structure with ZrC-SiC multi-coating as outer layer and ZrC-SiC-PyC ceramics as inner matrix was formed.ZrC and SiC rich areas were formed in the composites and on the coating surface due to the formation of Zr-Si intermetallic compounds in the RMI process.Mechanical tests showed that the average compression strength of the C/C-ZrC-SiC composites was 133.86 MPa,and the carbon fibers in the composites were not seriously damaged after the RMI process.
Xin Yang1,2，Zhean Su2，Qizhong Huang2，Xiao Fang2，Liyuan Chai1
1. School of Metallurgical Science and Engineering,Central South University2. State Key Laboratory of Powder Metallurgy,Central South University
摘 要：<正>To meet the increasing demand for advanced materials capable of operation over 2000℃for future thermal protection systems application,C/C—ZrC—SiC composites were fabricated by reactive melt infiltration（RMI） with Zr,Si mixed powders as raw materials.The structural evolution and formation mechanism of the C/C—ZrC -SiC composites were discussed,and the mechanical property of the as-prepared material was investigated by compression test.The results showed that after the RMI process,a special structure with ZrC-SiC multi-coating as outer layer and ZrC-SiC-PyC ceramics as inner matrix was formed.ZrC and SiC rich areas were formed in the composites and on the coating surface due to the formation of Zr-Si intermetallic compounds in the RMI process.Mechanical tests showed that the average compression strength of the C/C-ZrC-SiC composites was 133.86 MPa,and the carbon fibers in the composites were not seriously damaged after the RMI process.