Laser-based directed energy deposition of novel Sc/Zr-modified Al-Mg alloys: columnar-to-equiaxed transition and aging hardening behavior
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2021年第10期
论文作者：Zihong Wang Xin Lin Yao Tang Nan Kang Xuehao Gao Shuoqing Shi Weidong Huang
摘 要：The control of grain morphology is important in laser additive manufacturing（LAM）, as grain morphology further affects the hot cracking resistance, anisotropy, and strength–ductility synergy of materials. To develop a solidification-control solution and achieve columnar-to-equiaxed transition（CET） in Al-based alloys during LAM, Sc-and-Zr-modified Al-Mg alloys were processed via directed energy deposition（DED）.CET was achieved by introducing high potent primary Al3（Sc,Zr） nucleation sites ahead of the solidification interface. Furthermore, the relationship between the solidification control parameters and precipitation behavior of primary Al3（Sc,Zr） nucleation sites was established using the time-dependent nucleation theory. Then, the CET was studied according to the Hunt criterion. The results indicated that coarse columnar grain structure was still obtained at the inner region of the molten pool at low Sc/Zr contents owing to the effective suppression of the precipitation of the primary Al3（Sc,Zr） nucleation sites via rapid solidification during DED. In addition, the relatively low melt temperature at the fusion boundary unavoidably promoted the precipitation of primary Al3（Sc,Zr） nucleation sites, which resulted in a fine equiaxed grains band at the edge of the molten pool. As the Sc/Zr content increased, the solidification cooling rate was not sufficient to suppress the precipitation of the primary Al3（Sc,Zr） nucleation sites, and a fully equiaxed grain structure was obtained. Furthermore, the effect of the layer-by-layer manufacturing process on the subsequent precipitation strengthening of secondary Al3（Sc,Zr） precipitates was discussed.Both the remelting and subsequent aging during thermal cycling should be considered to achieve greater precipitation strengthening.
Zihong Wang1,2，Xin Lin1,2，Yao Tang1,2，Nan Kang1,2，Xuehao Gao1,2，Shuoqing Shi1,2，Weidong Huang1,2
1. State Key Laboratory of Solidification Processing, Northwestern Polytechnical University2. Key Laboratory of Metal High Performance Additive Manufacturing and Innovative Design, MIIT China, Northwestern Polytechnical University
摘 要：The control of grain morphology is important in laser additive manufacturing（LAM）, as grain morphology further affects the hot cracking resistance, anisotropy, and strength–ductility synergy of materials. To develop a solidification-control solution and achieve columnar-to-equiaxed transition（CET） in Al-based alloys during LAM, Sc-and-Zr-modified Al-Mg alloys were processed via directed energy deposition（DED）.CET was achieved by introducing high potent primary Al3（Sc,Zr） nucleation sites ahead of the solidification interface. Furthermore, the relationship between the solidification control parameters and precipitation behavior of primary Al3（Sc,Zr） nucleation sites was established using the time-dependent nucleation theory. Then, the CET was studied according to the Hunt criterion. The results indicated that coarse columnar grain structure was still obtained at the inner region of the molten pool at low Sc/Zr contents owing to the effective suppression of the precipitation of the primary Al3（Sc,Zr） nucleation sites via rapid solidification during DED. In addition, the relatively low melt temperature at the fusion boundary unavoidably promoted the precipitation of primary Al3（Sc,Zr） nucleation sites, which resulted in a fine equiaxed grains band at the edge of the molten pool. As the Sc/Zr content increased, the solidification cooling rate was not sufficient to suppress the precipitation of the primary Al3（Sc,Zr） nucleation sites, and a fully equiaxed grain structure was obtained. Furthermore, the effect of the layer-by-layer manufacturing process on the subsequent precipitation strengthening of secondary Al3（Sc,Zr） precipitates was discussed.Both the remelting and subsequent aging during thermal cycling should be considered to achieve greater precipitation strengthening.
关键词：