简介概要

Microstructures and hydrogen storage properties of as-cast and copper-mould-cast LaMg4Ni alloys

来源期刊:JOURNAL OF RARE EARTHS2014年第5期

论文作者:范燕平 彭显云 刘宝忠 宿太超 哈日巴拉

文章页码:434 - 438

摘    要:Phase compositions, morphologies and hydrogen storage properties of the as-cast and copper-mould-cast LaMg4Ni alloys were studied. The dehydriding onset temperature of the as-cast alloy hydride was about 500 K, which was at least 50 K higher than that of the copper-mould-cast one, and the copper-mould-cast alloy hydride had a faster dehydriding rate compared with as-cast one. Additionally, the copper-mould-cast alloy could uptake 2.85 wt.% hydrogen, which was 95.0% of saturated hydrogen storage capacity at room temperature. While only 1.80 wt.% hydrogen(60% of saturated capacity) was absorbed for the as-cast alloy under the same conditions. The reversible hydrogen storage capacities and plateau hydrogen pressures of the two alloys were close. X-ray diffractions and scanning electron microscopy results indicated that similar thermodynamic property of the two alloys should be ascribed to the same hydrogen storage phase, Mg and Mg2Ni. The better hydrogen sorption kinetics of copper-mould-cast alloy should be ascribed to the more uniform phase distribution compared with that of the as-cast one.

详情信息展示

Microstructures and hydrogen storage properties of as-cast and copper-mould-cast LaMg4Ni alloys

范燕平1,2,彭显云1,刘宝忠1,2,宿太超1,2,哈日巴拉1,2

1. School of Materials Science and Engineering, Henan Polytechnic University2. Cultivating Base for Key Laboratory of Environment-friendly Inorganic Materials in University of Henan Province, Henan Polytechnic University

摘 要:Phase compositions, morphologies and hydrogen storage properties of the as-cast and copper-mould-cast LaMg4Ni alloys were studied. The dehydriding onset temperature of the as-cast alloy hydride was about 500 K, which was at least 50 K higher than that of the copper-mould-cast one, and the copper-mould-cast alloy hydride had a faster dehydriding rate compared with as-cast one. Additionally, the copper-mould-cast alloy could uptake 2.85 wt.% hydrogen, which was 95.0% of saturated hydrogen storage capacity at room temperature. While only 1.80 wt.% hydrogen(60% of saturated capacity) was absorbed for the as-cast alloy under the same conditions. The reversible hydrogen storage capacities and plateau hydrogen pressures of the two alloys were close. X-ray diffractions and scanning electron microscopy results indicated that similar thermodynamic property of the two alloys should be ascribed to the same hydrogen storage phase, Mg and Mg2Ni. The better hydrogen sorption kinetics of copper-mould-cast alloy should be ascribed to the more uniform phase distribution compared with that of the as-cast one.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号