Hot Deformation and Dynamic Recrystallization Behavior of Austenite-Based Low-Density Fe–Mn–Al–C Steel
来源期刊：Acta Metallurgica Sinica2016年第5期
论文作者：Ya-Ping Li Ren-Bo Song Er-Ding Wen Fu-Qiang Yang
文章页码：441 - 449
摘 要：The hot deformation and dynamic recrystallization（DRX） behavior of austenite-based Fe–27Mn–11.5Al–0.95 C steel with a density of 6.55 g cm-3were investigated by compressive deformation at the temperature range of900–1150 °C and strain rate of 0.01–10 s-1. Typical DRX behavior was observed under chosen deformation conditions and yield-point-elongation-like effect caused by DRX of d-ferrite. The flow stress characteristics were determined by DRX of the d-ferrite at early stage and the austenite at later stage, respectively. On the basis of hyperbolic sine function and linear fitting, the calculated thermal activation energy for the experimental steel was 294.204 k J mol-1. The occurrence of DRX for both the austenite and the d-ferrite was estimated and plotted by related Zener–Hollomon equations. A DRX kinetic model of the steel was established by flow stress and peak strain without considering dynamic recovery and d-ferrite DRX. The effects of deformation temperature and strain rate on DRX volume fraction were discussed in detail. Increasing deformation temperature or strain rate contributes to DRX of both the austenite and the d-ferrite, whereas a lower strain rate leads to the austenite grains growth and the d-ferrite evolution, from banded to island-like structure.
Ya-Ping Li1，Ren-Bo Song1，Er-Ding Wen1，Fu-Qiang Yang2
1. School of Materials Science and Engineering, University of Science and Technology Beijing2. R&D Center, BAIC Motor Corporation LTD
摘 要：The hot deformation and dynamic recrystallization（DRX） behavior of austenite-based Fe–27Mn–11.5Al–0.95 C steel with a density of 6.55 g cm-3were investigated by compressive deformation at the temperature range of900–1150 °C and strain rate of 0.01–10 s-1. Typical DRX behavior was observed under chosen deformation conditions and yield-point-elongation-like effect caused by DRX of d-ferrite. The flow stress characteristics were determined by DRX of the d-ferrite at early stage and the austenite at later stage, respectively. On the basis of hyperbolic sine function and linear fitting, the calculated thermal activation energy for the experimental steel was 294.204 k J mol-1. The occurrence of DRX for both the austenite and the d-ferrite was estimated and plotted by related Zener–Hollomon equations. A DRX kinetic model of the steel was established by flow stress and peak strain without considering dynamic recovery and d-ferrite DRX. The effects of deformation temperature and strain rate on DRX volume fraction were discussed in detail. Increasing deformation temperature or strain rate contributes to DRX of both the austenite and the d-ferrite, whereas a lower strain rate leads to the austenite grains growth and the d-ferrite evolution, from banded to island-like structure.