Fatigue crack initiation for Al-Zn-Mg alloy welded joint

来源期刊:Acta Metallurgica Sinica2012年第3期

论文作者:陈真真

文章页码:235 - 240

摘    要:To investigate fatigue crack initiation characteristics of Al-Zn-Mg alloy welded joint, notched specimens were used in fatigue test for the base metal, welding bead and heat affected zone (HAZ). The fatigue fracture surface near the fatigue crack initiation site was observed by scanning electron microscope (SEM). The results show that the differences of fatigue crack initiation life among base metal, welding bead and HAZ are not obvious. Inhomogeneity in microstructure and mechanical performance of HAZ influences the fatigue crack initiation life. The ratio of fatigue crack initiation life (Ni) to fatigue failure life (Nf) for the base metal, welding bead and HAZ of A7N01 aluminium alloy welded joint are 26.32%, 40.21% and 60.67%, respectively. Fatigue crack initiation life can be predicted using a uniform model. Observation of fatigue fracture surfaces shows that for the welding bead a fatigue crack initiates from the smooth surface due to the welding process, the blowhole in HAZ causes fatigue crack and the crushed second phase particles play an important role in fatigue crack initiation for the base metal.

详情信息展示

Fatigue crack initiation for Al-Zn-Mg alloy welded joint

Liang ZHANG 1), Xuesong LIU 1), Linsen WANG 2), Ping WANG 1) and Hongyuan FANG 1) (1) State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China 2) Welding Process Section, Dongfang Boiler Group Co. Ltd., Zigong 643001, China)

摘 要:To investigate fatigue crack initiation characteristics of Al-Zn-Mg alloy welded joint, notched specimens were used in fatigue test for the base metal, welding bead and heat affected zone (HAZ). The fatigue fracture surface near the fatigue crack initiation site was observed by scanning electron microscope (SEM). The results show that the differences of fatigue crack initiation life among base metal, welding bead and HAZ are not obvious. Inhomogeneity in microstructure and mechanical performance of HAZ influences the fatigue crack initiation life. The ratio of fatigue crack initiation life (Ni) to fatigue failure life (Nf) for the base metal, welding bead and HAZ of A7N01 aluminium alloy welded joint are 26.32%, 40.21% and 60.67%, respectively. Fatigue crack initiation life can be predicted using a uniform model. Observation of fatigue fracture surfaces shows that for the welding bead a fatigue crack initiates from the smooth surface due to the welding process, the blowhole in HAZ causes fatigue crack and the crushed second phase particles play an important role in fatigue crack initiation for the base metal.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号