Application of Polymerizable Surfactant in the Preparation of Polystyrene/Nano-Fe3O4 Composite
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2010年第2期
论文作者：李瑞雪 赵建青 Hideyuki Otsuka Atsushi Takahara
文章页码：184 - 187
摘 要：Monooctadecyl maleate, as a polymerizable surfactant, was synthesized by the mono-esterification of maleic anhydride and octadecanol, and was utilized to surface-modify nano-Fe3O4 particles. A polymerizable magnetic fluid was obtained by directly dispersing modified nano-Fe3O4 particles into styrene monomer, and the polystyrene/nano-Fe3O4 composite was prepared through free radical polymerization of polymerizable magnetic fluid. The structure and dispersion status in different dispersion phases of modified nano-Fe3O4 particles were studied by Fourier transform infrared （FTIR） spectrometry, X-ray diffraction （XRD） and transmission electron microscopy （TEM）, respectively. The experimental results show that the nano-Fe3O4 particles modified by monooctadecyl maleate with the size of about 7-10 nm can be uniformly dispersed into styrene and fixed in the composite during the procedure of polymerization. Thermogravimetric analysis （TGA） and vibrating sample magnetometry （VSM） indicate that the thermal stability of polystyrene/nano-Fe3O4 composite is improved compared to that of pure polystyrene, and the composite is a sort of superparamagnetic materials.
李瑞雪1，赵建青1，Hideyuki Otsuka2，Atsushi Takahara2
1. College of Materials Science and Engineering, South China University of Technology2. Institute for Materials Chemistry and Engineering, Kyushu University, 744 Motooka, Nishi-ku, Fukuoka, 819-0395, Japan
摘 要：Monooctadecyl maleate, as a polymerizable surfactant, was synthesized by the mono-esterification of maleic anhydride and octadecanol, and was utilized to surface-modify nano-Fe3O4 particles. A polymerizable magnetic fluid was obtained by directly dispersing modified nano-Fe3O4 particles into styrene monomer, and the polystyrene/nano-Fe3O4 composite was prepared through free radical polymerization of polymerizable magnetic fluid. The structure and dispersion status in different dispersion phases of modified nano-Fe3O4 particles were studied by Fourier transform infrared （FTIR） spectrometry, X-ray diffraction （XRD） and transmission electron microscopy （TEM）, respectively. The experimental results show that the nano-Fe3O4 particles modified by monooctadecyl maleate with the size of about 7-10 nm can be uniformly dispersed into styrene and fixed in the composite during the procedure of polymerization. Thermogravimetric analysis （TGA） and vibrating sample magnetometry （VSM） indicate that the thermal stability of polystyrene/nano-Fe3O4 composite is improved compared to that of pure polystyrene, and the composite is a sort of superparamagnetic materials.