Microstructure and mechanical property of MIM 418 superalloy
来源期刊：Rare Metals2018年第1期
论文作者：Fu-Bao Yang Yan-Hong Jing Dan Li Lin Zhang Da-Quan Li Qiang Zhu
文章页码：35 - 39
摘 要：In this study, the influence of hot isostatic pressing（HIP） process on the 418 alloy produced by metal injection molding（MIM） technique（named as MIM 418）was investigated based on the characteristic analysis of 418 alloy powder. And comparison analysis of the microstructure and mechanical property between the MIM 418 and as-cast 418 alloys was performed by scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS）,and X-ray diffraction（XRD）. The results show that MIM418 alloy exhibits fine grain（30 μm） and uniform microstructure. The defects existing in MIM 418 alloy formed during sintering process can be eliminated through HIP treatment, and the relative density increases from97.0 % to 99.5 %. The mechanical property can be improved significantly because of the elimination of defects, and the tensile strength and elongation are1,271 MPa and 16.8 %, respectively, which are increased by 34.5 % and 180 % compared with K418 alloy after solution heat treatment.
Fu-Bao Yang1，Yan-Hong Jing1，Dan Li2，Lin Zhang2，Da-Quan Li1，Qiang Zhu1
1. National Engineering and Technology Research Center for Nonferrous Metal Matrix Composites, General Research Institute for Nonferrous Metals2. Powder Metallurgy Research Institute, University of Science and Technology Beijing
摘 要：In this study, the influence of hot isostatic pressing（HIP） process on the 418 alloy produced by metal injection molding（MIM） technique（named as MIM 418）was investigated based on the characteristic analysis of 418 alloy powder. And comparison analysis of the microstructure and mechanical property between the MIM 418 and as-cast 418 alloys was performed by scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS）,and X-ray diffraction（XRD）. The results show that MIM418 alloy exhibits fine grain（30 μm） and uniform microstructure. The defects existing in MIM 418 alloy formed during sintering process can be eliminated through HIP treatment, and the relative density increases from97.0 % to 99.5 %. The mechanical property can be improved significantly because of the elimination of defects, and the tensile strength and elongation are1,271 MPa and 16.8 %, respectively, which are increased by 34.5 % and 180 % compared with K418 alloy after solution heat treatment.
关键词：