Adsorption of Au（Ⅲ） by amino-modified monodispersed PGMA microspheres and deposition of gold nanoparticles
来源期刊：Rare Metals2018年第3期
论文作者：Fu-Chun Wang Jun-Mei Zhao Wan-Kun Wang Zi-Zheng Tong
文章页码：196 - 203
摘 要：Monodispersed poly（glycidyl methacrylate）（PGMA） microspheres with various amounts of amino groups（PGMA-NH2） were used to adsorb Au（Ⅲ） from simulated wastewaters. Gold nanoparticle-coated PGMA functional microspheres can be directly obtained via the adsorption process. The adsorption kinetics follows pseudo-second model, and 10 min is enough for reaching at equilibrium. The adsorption isotherm follows Langmuir model, and the adsorption amounts for Au（Ⅲ） are 8.25 and 21.75 mol·kg-1 at 298 and 328 K, respectively. The relative separation coefficients between Au（Ⅲ）, Pt（Ⅵ）, Pd（Ⅱ）and Co（Ⅱ）, Cu（Ⅱ）; Ni（Ⅱ）, Fe（Ⅲ） are all higher than 100 when 1 < pH < 3. Furthermore, the characterization analysis of X-ray diffraction（XRD）, thermogravimetrydifferential scanning calorimetry（TG-DSC）, scanning electron microscopy-energy dispersive spectroscopy（SEM-EDS）, transmission electron microscopy（TEM） and Fourier transform infrared spectroscopy（FTIR） confirms that AuCl4-has been reduced to Au0 nanoparticles and deposited onto the surface of PGMA-NH2. The current work shows a good prospect for PGMA-NH2 to be a valid adsorbent for the recovery of gold and the possible fabrication of gold nanoparticles by reduction-deposition process without any reductant.
Fu-Chun Wang1，Jun-Mei Zhao2，Wan-Kun Wang1，Zi-Zheng Tong2
1. School of Materials and Metallurgical Engineering,Guizhou Institute of Technology2. Institute of Process Engineering,Chinese Academy of Sciences
摘 要：Monodispersed poly（glycidyl methacrylate）（PGMA） microspheres with various amounts of amino groups（PGMA-NH2） were used to adsorb Au（Ⅲ） from simulated wastewaters. Gold nanoparticle-coated PGMA functional microspheres can be directly obtained via the adsorption process. The adsorption kinetics follows pseudo-second model, and 10 min is enough for reaching at equilibrium. The adsorption isotherm follows Langmuir model, and the adsorption amounts for Au（Ⅲ） are 8.25 and 21.75 mol·kg-1 at 298 and 328 K, respectively. The relative separation coefficients between Au（Ⅲ）, Pt（Ⅵ）, Pd（Ⅱ）and Co（Ⅱ）, Cu（Ⅱ）; Ni（Ⅱ）, Fe（Ⅲ） are all higher than 100 when 1 < pH < 3. Furthermore, the characterization analysis of X-ray diffraction（XRD）, thermogravimetrydifferential scanning calorimetry（TG-DSC）, scanning electron microscopy-energy dispersive spectroscopy（SEM-EDS）, transmission electron microscopy（TEM） and Fourier transform infrared spectroscopy（FTIR） confirms that AuCl4-has been reduced to Au0 nanoparticles and deposited onto the surface of PGMA-NH2. The current work shows a good prospect for PGMA-NH2 to be a valid adsorbent for the recovery of gold and the possible fabrication of gold nanoparticles by reduction-deposition process without any reductant.