铝镁硅合金阳极氧化膜性能的研究

来源期刊:中南大学学报(自然科学版)1990年第3期

论文作者:田荣璋 蒋次雪 龚鸣明

文章页码:277 - 282

关键词:铝合金; 阳极处理; 阳极氧化; 耐蚀性/膜极氧化膜

Key words:alumininum-alloys; anodization; anodized oxidationm; corrosion resistance/anodizatino film

摘    要:本文通过6063合金阳极氧化膜的连续性实验,透射电子显微分析等手段,研究了稀土、镁、硅对阳极氧化膜的厚度、耐蚀性和显微硬度的影响。实验结果表明:在60min内进行阳极氧化,氧化膜的厚度与氧化时间成直线关系,合全元素对膜厚影响不大;稀土元素能使6063合全氧化膜中缺陷减少及膜的连续性增加,氧化膜中针孔变小且孔分布均匀,因而明显地提高了6063合金的耐蚀性和显微硬度。

Abstract: By means of examination of the continuity of the oxidic film,TEM and soon,the influence of RE,Mg,and Si on the anodized film thickness,corrosionresistance and micro-hardness was studied.The experimental results showed thatthe anodized film thickness is linear with the anodizing time within the range of60 min.The RE could obviously increase the corrosion-resistance and micro-hardness of alloy 6063 by decreasing defects and pore size in the film,by imprvoingthe continuity of the film,and by making the pore well-distributed.

详情信息展示

<上一页 1 下一页 >

相关论文

  • 暂无!

相关知识点

  • 暂无!

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号