Grain refining potency of LaB6 on aluminum alloy
来源期刊：Journal of Rare Earths2012年第11期
论文作者：李鹏廷 田文婕 王栋 刘相法
文章页码：1172 - 1176
摘 要：Al-LaB6 alloy was successfully prepared by aluminum melt reaction method.Microstructure analysis of this alloy was carried out by field emission scanning electron microscopy（FESEM）,Raman spectroscopy and transmission electron microscopy（TEM）.It was found that cubic LaB6 particles were highly dispersed in aluminum matrix with a uniform edge length of about 4.5 μm.Grain refining potency of LaB6 on commercial pure aluminum was also investigated.It was shown that LaB6 could act as an effective and stable nucleation substrate for α-Al during solidification process,due to their crystallographic similarity.The coarse grains of commercial pure aluminum were obviously refined to small equiaxed ones by addition of 0.5% Al-5LaB6 alloy at 720℃.
李鹏廷，田文婕，王栋，刘相法
Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials,Ministry of Education,Shandong University
摘 要：Al-LaB6 alloy was successfully prepared by aluminum melt reaction method.Microstructure analysis of this alloy was carried out by field emission scanning electron microscopy（FESEM）,Raman spectroscopy and transmission electron microscopy（TEM）.It was found that cubic LaB6 particles were highly dispersed in aluminum matrix with a uniform edge length of about 4.5 μm.Grain refining potency of LaB6 on commercial pure aluminum was also investigated.It was shown that LaB6 could act as an effective and stable nucleation substrate for α-Al during solidification process,due to their crystallographic similarity.The coarse grains of commercial pure aluminum were obviously refined to small equiaxed ones by addition of 0.5% Al-5LaB6 alloy at 720℃.
关键词：