Compressive Strength and Interface Microstructure of PCBN Grains Brazed with High-Frequency Induction Heating Method
来源期刊：Acta Metallurgica Sinica2017年第7期
论文作者：Ye-Jun Zhu Wen-Feng Ding Ze-Yu Zhao Yu-Can Fu Hong-Hua Su
文章页码：641 - 649
摘 要：In order to prepare monolayer brazed superabrasive wheels, the polycrystalline cubic boron nitride（PCBN）grains were brazed to AISI 1045 steel matrix with Ag–Cu–Ti filler alloy using the high-frequency induction heating technique. The compressive strengths of brazed grains were measured. Morphology, chemical composition and phase component of the brazing resultant around PCBN grain were also characterized. The results show that the maximum compressive strength of brazed grains is obtained in the case of brazing temperature of 965 °C, which does not decrease the original grain strength. Strong joining between Ag–Cu–Ti alloy and PCBN grains is dependent on the brazing resultants,such as TiB2, TiN and AlTi3, the formation mechanism of which is also discussed. Under the given experimental conditions, the optimum heating parameters were determined to be current magnitude of 24 A and scanning speed of0.5 mm/s. Finally, the brazing-induced residual tensile stress, which has a great influence on the grain fracture behavior in grinding, was determined through finite element analysis.
Ye-Jun Zhu，Wen-Feng Ding，Ze-Yu Zhao，Yu-Can Fu，Hong-Hua Su
College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics
摘 要：In order to prepare monolayer brazed superabrasive wheels, the polycrystalline cubic boron nitride（PCBN）grains were brazed to AISI 1045 steel matrix with Ag–Cu–Ti filler alloy using the high-frequency induction heating technique. The compressive strengths of brazed grains were measured. Morphology, chemical composition and phase component of the brazing resultant around PCBN grain were also characterized. The results show that the maximum compressive strength of brazed grains is obtained in the case of brazing temperature of 965 °C, which does not decrease the original grain strength. Strong joining between Ag–Cu–Ti alloy and PCBN grains is dependent on the brazing resultants,such as TiB2, TiN and AlTi3, the formation mechanism of which is also discussed. Under the given experimental conditions, the optimum heating parameters were determined to be current magnitude of 24 A and scanning speed of0.5 mm/s. Finally, the brazing-induced residual tensile stress, which has a great influence on the grain fracture behavior in grinding, was determined through finite element analysis.