Design and achieving of multicolor upconversion emission based on rare-earth doped tellurite glasses
来源期刊:Journal of Rare Earths2014年第5期
论文作者:邢明铭 马运北 罗昔贤 付姚 姜涛 汪红 段小龙
文章页码:394 - 398
摘 要:Yb3+/Tm3+ co-doped and Yb3+/Ho3+/Tm3+ tri-doped tellurite glasses were synthesized by fusing the mixture of TeO2, PbF2, AlF3, BaF2, Yb2O3, Tm2O3 and Ho2O3 in a corundum crucible at 850 oC for 20 min. The synthesized glasses were characterized by upconversion emission spectra under the excitation of 980 nm laser, and the emission colors were investigated according to the CIE-1931 standards. The results indicated that Yb3+/Tm3+ co-doped tellurite glass exhibited blue upconversion emission with favorable color coordinates of(0.20, 0.07). Yb3+, Ho3+ and Tm3+ tri-doped tellurite glasses presented white upconversion luminescence under a single 980 nm laser excitation. Moreover, a very wide range of emission colors could be tuned by altering Ho3+ concentration. Combining the contribution of adjusting Ho3+ concentration and pump power, near equal energy white light was obtained.
邢明铭,马运北,罗昔贤,付姚,姜涛,汪红,段小龙
Physics Department,Dalian Maritime University
摘 要:Yb3+/Tm3+ co-doped and Yb3+/Ho3+/Tm3+ tri-doped tellurite glasses were synthesized by fusing the mixture of TeO2, PbF2, AlF3, BaF2, Yb2O3, Tm2O3 and Ho2O3 in a corundum crucible at 850 oC for 20 min. The synthesized glasses were characterized by upconversion emission spectra under the excitation of 980 nm laser, and the emission colors were investigated according to the CIE-1931 standards. The results indicated that Yb3+/Tm3+ co-doped tellurite glass exhibited blue upconversion emission with favorable color coordinates of(0.20, 0.07). Yb3+, Ho3+ and Tm3+ tri-doped tellurite glasses presented white upconversion luminescence under a single 980 nm laser excitation. Moreover, a very wide range of emission colors could be tuned by altering Ho3+ concentration. Combining the contribution of adjusting Ho3+ concentration and pump power, near equal energy white light was obtained.
关键词: