Growth and passivation of aluminum etch tunnels at on-off controlling direct current in 6 wt.% HCI solution
来源期刊：Rare Metals2008年第2期
论文作者：WANG Mei HE Yedong Beijing Key Laboratory for Corrosion,Erosion and Surface Technique,University of Science and Technology Beijing,Beijing ,China
文章页码：205 - 209
摘 要：<正>Growth and passivation of tunnels within Al foil by on-off controlling DC etching in 6 wt.% HCl solution has been investigated.It was found that,in a given etchant solution at a special temperature,the longest tunnel length was only a function of the turn-on interval of DC.The po- tential of Al foil broke at on-off controlling DC by the result from anode polarization curves and potential-time （E-t） responding curves. When DC was switched on,the potential increased abruptly over pitting potential,leading to nucleation of pits at the surface and the growth of tunnels at special length.When DC was switched off,the potential decreased rapidly to a passive value,leading to stoppage of nucleation and death of tunnels.By this way,the longest tunnel length can be controlled and a non-piercing layer can be obtained.Hence,etching of Al foil at this current is beneficial for maintaining a good mechanical strength.
WANG Mei HE Yedong Beijing Key Laboratory for Corrosion,Erosion and Surface Technique,University of Science and Technology Beijing,Beijing 100083,China
摘 要：<正>Growth and passivation of tunnels within Al foil by on-off controlling DC etching in 6 wt.% HCl solution has been investigated.It was found that,in a given etchant solution at a special temperature,the longest tunnel length was only a function of the turn-on interval of DC.The po- tential of Al foil broke at on-off controlling DC by the result from anode polarization curves and potential-time （E-t） responding curves. When DC was switched on,the potential increased abruptly over pitting potential,leading to nucleation of pits at the surface and the growth of tunnels at special length.When DC was switched off,the potential decreased rapidly to a passive value,leading to stoppage of nucleation and death of tunnels.By this way,the longest tunnel length can be controlled and a non-piercing layer can be obtained.Hence,etching of Al foil at this current is beneficial for maintaining a good mechanical strength.
关键词：