Microstructure and Tribological Properties of Laser Clad Ni-Ag/TiC Composite Coating
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2014年第2期
论文作者：朱流 罗来马 WU Yucheng CHENG Jigui
文章页码：242 - 245
摘 要：Ni-Ag/TiC composite coating was prepared on the 45 steel substrates by means of laser cladding. Microstructure and wear properties of composite coatings were analyzed using optical microscopy, field emission scanning electron microscopy and wear machine. The experimental results show that defects, such as cracks and pores, do not occur in the laser-cladded Ni-Ag/TiC composite coating and 45 steel substrate, and they present good metallurgical bonding between them. Compared with Ni/TiC composite coating, microhardness values of the two coatings do not present evident differences. The wear experiment result shows that Ni-Ag/TiC composite coated with Ag possesses low friction coefficient and good wear resistance compared with Ni/TiC composite coating.
朱流1，罗来马2，WU Yucheng2，CHENG Jigui2
1. Department of Mechanical Engineering, Taizhou University2. College of Material Science and Engineering,Hefei University of Technology
摘 要：Ni-Ag/TiC composite coating was prepared on the 45 steel substrates by means of laser cladding. Microstructure and wear properties of composite coatings were analyzed using optical microscopy, field emission scanning electron microscopy and wear machine. The experimental results show that defects, such as cracks and pores, do not occur in the laser-cladded Ni-Ag/TiC composite coating and 45 steel substrate, and they present good metallurgical bonding between them. Compared with Ni/TiC composite coating, microhardness values of the two coatings do not present evident differences. The wear experiment result shows that Ni-Ag/TiC composite coated with Ag possesses low friction coefficient and good wear resistance compared with Ni/TiC composite coating.