600 Mesh Silicon Carbide Corona Protection Varnish with EPOXY/OMMT Nano-composite Adhesive
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2016年第4期
论文作者：胡春秀 ZHAO Yingnan HOU Haibo ZHANG Xiaohong
文章页码：818 - 822
摘 要：A new corona protection varnish was prepared by using epoxy/montmorillonite nanocomposite and pure epoxy resin as adhesives respectively.The adhesive with different amounts of organic montmorillonite（OMMT） was mixed with 1200 mesh silicon carbide（Si C） by different weight ratios.The surface states of the varnishes with various adhesives were observed by powerful optical microscope.Some properties of the varnishes were analyzed during the enduring time under 5kV/cm DC,such as the relation of change in nonlinear coefficient,natural surface resistivity,and surface temperature variation.The results showed that the amounts of OMMT had little effect on the natural surface resistance of the varnish but had important influence on the nonlinear property of the varnish.When the range of the OMMT content was 2wt% to 6wt%,the nonlinear coefficient of all materials with epoxy/OMMT nano-composite adhesive was higher than that with pure epoxy resin adhesive.The surface temperature of the varnish with epoxy/OMMT nanocomposite adhesive was all lower than that with the pure epoxy resin adhesive under high electrical field strength.
胡春秀1，ZHAO Yingnan1，HOU Haibo2，ZHANG Xiaohong2
1. Harbin Research Institute of Large Electric Machinery2. Key Laboratory of Engineering Dielectrics and Its Application,Harbin University of Science and Technology
摘 要：A new corona protection varnish was prepared by using epoxy/montmorillonite nanocomposite and pure epoxy resin as adhesives respectively.The adhesive with different amounts of organic montmorillonite（OMMT） was mixed with 1200 mesh silicon carbide（Si C） by different weight ratios.The surface states of the varnishes with various adhesives were observed by powerful optical microscope.Some properties of the varnishes were analyzed during the enduring time under 5kV/cm DC,such as the relation of change in nonlinear coefficient,natural surface resistivity,and surface temperature variation.The results showed that the amounts of OMMT had little effect on the natural surface resistance of the varnish but had important influence on the nonlinear property of the varnish.When the range of the OMMT content was 2wt% to 6wt%,the nonlinear coefficient of all materials with epoxy/OMMT nano-composite adhesive was higher than that with pure epoxy resin adhesive.The surface temperature of the varnish with epoxy/OMMT nanocomposite adhesive was all lower than that with the pure epoxy resin adhesive under high electrical field strength.