Joining Performance and Microstructure of the 2024/7075 Aluminium Alloys Welded Joints by Vaporizing Foil Actuator Welding
来源期刊:Journal Of Wuhan University Of Technology Materials Science Edition2019年第2期
论文作者:孟正华 WANG Xu GUO Wei HU Zhili Anupam Vivek HUA Lin Glenn S DAEHN
文章页码:368 - 372
摘 要:Vaporizing foil actuator welding(VFAW) was used for joining 2024-T3 and 7075-T6 aluminum alloy sheets, and the resulting joint microstructure was analyzed. 2024/7075 aluminum alloy pairs with suitable processing parameters can be prepared by using VFAW. Dynamic preform addresses the poor formability problem of target material and advantage of VFAW on dissimilar materials in some conditions. But with standoff sheet inserting in the flyer and target, 2024/7075 welded pairs gets the better weld strength, compared with flyer preformed method. The microstructure of the circular weld area of the welded joint showed a wave interface, in which a thin melt layer formed at the center and edge parts. The crystal grains near the bonding interface were remarkably elongated and refined. Therefore, the joining of the 2024/7075 pairs was facilitated through plastic forming and melting.
孟正华1,2,WANG Xu1,GUO Wei1,HU Zhili1,Anupam Vivek3,HUA Lin1,Glenn S DAEHN3
1. Hubei Key Laboratory of Advanced Technology for Automotive Components, Wuhan University of Technology2. State Key Laboratory of Advanced Design and Manufacturing for Vehicle Body, Hunan University3. Department of Materials Science and Engineering, The Ohio State University
摘 要:Vaporizing foil actuator welding(VFAW) was used for joining 2024-T3 and 7075-T6 aluminum alloy sheets, and the resulting joint microstructure was analyzed. 2024/7075 aluminum alloy pairs with suitable processing parameters can be prepared by using VFAW. Dynamic preform addresses the poor formability problem of target material and advantage of VFAW on dissimilar materials in some conditions. But with standoff sheet inserting in the flyer and target, 2024/7075 welded pairs gets the better weld strength, compared with flyer preformed method. The microstructure of the circular weld area of the welded joint showed a wave interface, in which a thin melt layer formed at the center and edge parts. The crystal grains near the bonding interface were remarkably elongated and refined. Therefore, the joining of the 2024/7075 pairs was facilitated through plastic forming and melting.