Effect of SrCO3 addition on the dynamic compressive strength of ZTA
来源期刊：International Journal of Minerals Metallurgy and Materials2016年第4期
论文作者：Ali Arab Roslan Ahmad Zainal Arifin Ahmad
文章页码：481 - 489
摘 要：Ceramic parts usually experience dynamic load in armor applications. Therefore, studying the dynamic behaviors of ceramics is important. Limited data are available on the dynamic behaviors of ceramics; thus, it is helpful to predict the dynamic strength of ceramics on the basis of their mechanical properties. In this paper, the addition of SrCO3 into zirconia-toughened alumina（ZTA） was demonstrated to improve the fracture toughness of ZTA due to the formation of the SrAl12O19（SA6） phase. The porosity of ZTA was found to be increased by the addition of SrCO3. These newly formed pores served as the nucleation sites of cracks under dynamic load; these cracks eventually coalesced to form damaged zones in the samples. Although the KIC values of the samples were improved, the dynamic strength was not enhanced because of the increase in porosity; in fact, the dynamic strength of ZTA ceramics decreased with the addition of SrCO3.
Ali Arab1,2，Roslan Ahmad1，Zainal Arifin Ahmad2
1. School of Mechanical Engineering, Universiti Sains Malaysia, Engineering Campus2. Structural Materials Niche Area, School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, Engineering Campus
摘 要：Ceramic parts usually experience dynamic load in armor applications. Therefore, studying the dynamic behaviors of ceramics is important. Limited data are available on the dynamic behaviors of ceramics; thus, it is helpful to predict the dynamic strength of ceramics on the basis of their mechanical properties. In this paper, the addition of SrCO3 into zirconia-toughened alumina（ZTA） was demonstrated to improve the fracture toughness of ZTA due to the formation of the SrAl12O19（SA6） phase. The porosity of ZTA was found to be increased by the addition of SrCO3. These newly formed pores served as the nucleation sites of cracks under dynamic load; these cracks eventually coalesced to form damaged zones in the samples. Although the KIC values of the samples were improved, the dynamic strength was not enhanced because of the increase in porosity; in fact, the dynamic strength of ZTA ceramics decreased with the addition of SrCO3.