Scaling Behavior and Magnetic Properties for Smx Co5 Films

来源期刊:Journal of Rare Earths2006年第S1期

论文作者:李加新 王锋 赖恒 郑卫峰 贾翠红 盖荣权 黄志高

文章页码:266 - 269

摘    要:<正>SmxCo5(x = 1.3, 0.7, 0.4) thin films were prepared by magnetron co-sputtering technique. The samples were annealed at 723 K under Ar atmosphere. The annealed time was chosen as 30 min. The hysteresis loops of the samples were measured under the ac applied magnetic field with the period Tp(2πω) , H(t) = H0sin(ωt), by vibrating sample magnetometer (VSM). The experimental results indicate that, (1) the average hysteresis loop areas as functions of the values of H0 andωdisplay a power scaling law with the exponents, A = A0 + H0αωβ; (2) the x composition of SmxCo5 film has evident effect on the scaling behavior and magnetic properties; (3) the anisotropy scaling exponents exist clearly in the anisotropy SmxCo5 thin films. Moreover, the scaling behavior of the anisotropy magnetic film was also simulated with Monte Carlo method. The simulated results are consistent with the experimental fact.

详情信息展示

Scaling Behavior and Magnetic Properties for Smx Co5 Films

李加新,王锋,赖恒,郑卫峰,贾翠红,盖荣权,黄志高

摘 要:<正>SmxCo5(x = 1.3, 0.7, 0.4) thin films were prepared by magnetron co-sputtering technique. The samples were annealed at 723 K under Ar atmosphere. The annealed time was chosen as 30 min. The hysteresis loops of the samples were measured under the ac applied magnetic field with the period Tp(2πω) , H(t) = H0sin(ωt), by vibrating sample magnetometer (VSM). The experimental results indicate that, (1) the average hysteresis loop areas as functions of the values of H0 andωdisplay a power scaling law with the exponents, A = A0 + H0αωβ; (2) the x composition of SmxCo5 film has evident effect on the scaling behavior and magnetic properties; (3) the anisotropy scaling exponents exist clearly in the anisotropy SmxCo5 thin films. Moreover, the scaling behavior of the anisotropy magnetic film was also simulated with Monte Carlo method. The simulated results are consistent with the experimental fact.

关键词:

<上一页 1 下一页 >

有色金属在线官网  |   会议  |   在线投稿  |   购买纸书  |   科技图书馆

中南大学出版社 技术支持 版权声明   电话:0731-88830515 88830516   传真:0731-88710482   Email:administrator@cnnmol.com

互联网出版许可证:(署)网出证(京)字第342号   京ICP备17050991号-6      京公网安备11010802042557号