Effects of Thickness on Mechanical Properties of 2D C/SiC Torque Tube
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2019年第5期
论文作者：赵晖 ZHANG Litong CHEN Bo ZHANG Jiaxin
文章页码：1049 - 1054
摘 要：Different failure modes and morphologies were found in the chemical vapor infiltration（CVI） 2 D C/SiC torque tubes with different thickness. To characterize the density and porosity of the ceramic matrix composite（CMC） torque tube, a CT test was conducted. The archimedes drainage method was used to measure the density and porosity, and by adopting FEM software, the stress distribution and failure strength of the ceramic matrix composite torque tubes were calculated. A universal material test machine was used to implement torsional tests. Different torsional behaviors of CMC torque tubes with two different thicknesses were showed in the stress-strain curves. To analyze the predominant failure factors, SEM was used to observe the failure morphologies and cracks. 5 mm thickness CMC torque tube has reasonable fracture morphologies and a higher maximum shear strength and modulus.
赵晖，ZHANG Litong，CHEN Bo，ZHANG Jiaxin
Science and Technology on Thermostructure Composite Materials Laboratory, Northwestern Polytechnical University
摘 要：Different failure modes and morphologies were found in the chemical vapor infiltration（CVI） 2 D C/SiC torque tubes with different thickness. To characterize the density and porosity of the ceramic matrix composite（CMC） torque tube, a CT test was conducted. The archimedes drainage method was used to measure the density and porosity, and by adopting FEM software, the stress distribution and failure strength of the ceramic matrix composite torque tubes were calculated. A universal material test machine was used to implement torsional tests. Different torsional behaviors of CMC torque tubes with two different thicknesses were showed in the stress-strain curves. To analyze the predominant failure factors, SEM was used to observe the failure morphologies and cracks. 5 mm thickness CMC torque tube has reasonable fracture morphologies and a higher maximum shear strength and modulus.
关键词：