Effect of different additives on the properties of lithium alanate
来源期刊：International Journal of Minerals Metallurgy and Materials2008年第6期
论文作者：I.S. Humail
文章页码：786 - 790
摘 要：LiAlH4 doped with Ni and Ce（SO4）2 additives and the effect of doping on temperature and hydrogen release were studied by pressure-content-temperature （PCT） experiment and X-ray diffraction （XRD） analysis. It is indicated that doping with Ni induces a significant decrease in temperature in the first step and LiAlH4 doped with 1mol% Ni presents the most absorption of hydrogen. Doping with Ce（SO4）2 also causes a marked decrease, while the amount of hydrogen release changes only slightly. The results from X-ray diffraction analysis show that doping does not cause any structural change; Ni and Ce-containing phases are not observed at room temperature or even at 250°C.
I.S. Humail
School of Materials Science and Engineering,University of Science and Technology Beijing
摘 要：LiAlH4 doped with Ni and Ce（SO4）2 additives and the effect of doping on temperature and hydrogen release were studied by pressure-content-temperature （PCT） experiment and X-ray diffraction （XRD） analysis. It is indicated that doping with Ni induces a significant decrease in temperature in the first step and LiAlH4 doped with 1mol% Ni presents the most absorption of hydrogen. Doping with Ce（SO4）2 also causes a marked decrease, while the amount of hydrogen release changes only slightly. The results from X-ray diffraction analysis show that doping does not cause any structural change; Ni and Ce-containing phases are not observed at room temperature or even at 250°C.
关键词：