Luminescent Properties of Ca2 Y8 ( SiO4 ) 6O2:Eu3 + Phosphors Prepared by Spray Pyrolysis Process
来源期刊：JOURNAL OF RARE EARTHS2004年增刊第1期
论文作者：Shen Weiying Lin Jun
Key words：silicate oxyapatite; spray pyrolysis; luminescence; europium; spherical phosphor;
Abstract: Using CaCO3, metal oxides (all dissolved by nitric acid) and tetraethoxysilane Si (OC2H5 )4 (TEOS) as the main starting materials, Ca2Y8 (SiO4 )6O2: Eu3+ phosphors were synthesized by spray pyrolysis.X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting phosphors.The results of XRD indicated that the 1000 ℃ annealed powders crystallize with the silicate oxyapatite structure.SEM study revealed that the phosphors consist of spherical particles with an average size of about 1 ～ 3 μm.In the crystalline Ca2 Y8 (SiO4)6O2: Eu3+ phosphor, the Eu3+ shows its characteristic emission corresponding to 5 D0 - 7 FJ ( J = 0, 1,2, 3, 4) transitions, with 5D0 - 7 F2 red emission (613 nm) as the most prominent group, agreeing well with the structure of the host material.
Shen Weiying1，Lin Jun1
(1.Key Laboratory of Rare Earth Chemistry and Physics, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China)
Abstract:Using CaCO3, metal oxides (all dissolved by nitric acid) and tetraethoxysilane Si (OC2H5 )4 (TEOS) as the main starting materials, Ca2Y8 (SiO4 )6O2: Eu3+ phosphors were synthesized by spray pyrolysis.X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting phosphors.The results of XRD indicated that the 1000 ℃ annealed powders crystallize with the silicate oxyapatite structure.SEM study revealed that the phosphors consist of spherical particles with an average size of about 1 ～ 3 μm.In the crystalline Ca2 Y8 (SiO4)6O2: Eu3+ phosphor, the Eu3+ shows its characteristic emission corresponding to 5 D0 - 7 FJ ( J = 0, 1,2, 3, 4) transitions, with 5D0 - 7 F2 red emission (613 nm) as the most prominent group, agreeing well with the structure of the host material.
Key words:silicate oxyapatite; spray pyrolysis; luminescence; europium; spherical phosphor;