Influence of Solidiflcation Rate on Microstructures of Cast Strips and Corresponding Sintered NdFeB Magnets
来源期刊:Journal of Rare Earths2006年第S1期
论文作者:徐静 颜世宏 于敦波 李宗安 李世鹏 李红卫
文章页码:306 - 309
摘 要:<正>The influences of solidification rate on the microstructures of cast strips and corresponding sintered NdFeB magnets were investigated. The experimental results show that the volume fraction and size of columnar grains vary with the wheel speed V, and the fraction is highest to more than 90% with 3.5μm in average width at V = 2m·s-1. The reasons for the improved magnetic performance were discussed based on the micromagnetic theory and microstructure analyses of the strips and sintered magnets. The magnetic properties of sintered NdFeB magnets made from the (Nd,Dy)13.0(Fe,Ga, Al)80.5B6.5 cast strip which was obtained at V = 2 m·s-1 are as follows: Br = 1.15 T( 11.25 kG), iHc = 2799 kA·m-1 (35.2 kOe) and (BH)max = 242 kJ·m-3(30.35 MGOe).
徐静,颜世宏,于敦波,李宗安,李世鹏,李红卫
摘 要:<正>The influences of solidification rate on the microstructures of cast strips and corresponding sintered NdFeB magnets were investigated. The experimental results show that the volume fraction and size of columnar grains vary with the wheel speed V, and the fraction is highest to more than 90% with 3.5μm in average width at V = 2m·s-1. The reasons for the improved magnetic performance were discussed based on the micromagnetic theory and microstructure analyses of the strips and sintered magnets. The magnetic properties of sintered NdFeB magnets made from the (Nd,Dy)13.0(Fe,Ga, Al)80.5B6.5 cast strip which was obtained at V = 2 m·s-1 are as follows: Br = 1.15 T( 11.25 kG), iHc = 2799 kA·m-1 (35.2 kOe) and (BH)max = 242 kJ·m-3(30.35 MGOe).
关键词: