Investigation on the icosahedral quasicrystal phase in Mg70.8Zn28Nd1.2 alloy
来源期刊：Journal of Rare Earths2009年第2期
论文作者：张金山 严杰 韩富银 梁伟 许春香 周翠兰
文章页码：264 - 269
摘 要：Mg70.8Zn28Nd1.2 （mole fraction） alloy containing icosahedral quasicrystal phase （I-phase） was prepared under conventional metal casting conditions. The microstructure, phase constitution and phase structure of the alloy were investigated by means of scanning electron microscopy （SEM）, X-ray diffraction （XRD）, energy dispersive spectrometer （EDS） and transmission electron microscopy （TEM）. The results showed that the spherical phase in Mg70.8Zn28Nd1.2 alloy was a simple icosahedral quasicrystal with stoichiometric composition of Mg40Zn55Nd5 and quasi-lattice of 0.525 nm. In this research, the as-cast microstructure of Mg70.8Zn28Nd1.2 alloy mainly consisted of Mg40Zn55Nd5 icosahedral quasicrystal phase and Mg7Zn3 columnar crystal matrix. In the growing process of Mg40Zn55Nd5 icosahedral quasicrystal phase, the growth morphology mainly depended on interface energy, adsorption effect of Nd and cooling rate.
张金山，严杰，韩富银，梁伟，许春香，周翠兰
摘 要：Mg70.8Zn28Nd1.2 （mole fraction） alloy containing icosahedral quasicrystal phase （I-phase） was prepared under conventional metal casting conditions. The microstructure, phase constitution and phase structure of the alloy were investigated by means of scanning electron microscopy （SEM）, X-ray diffraction （XRD）, energy dispersive spectrometer （EDS） and transmission electron microscopy （TEM）. The results showed that the spherical phase in Mg70.8Zn28Nd1.2 alloy was a simple icosahedral quasicrystal with stoichiometric composition of Mg40Zn55Nd5 and quasi-lattice of 0.525 nm. In this research, the as-cast microstructure of Mg70.8Zn28Nd1.2 alloy mainly consisted of Mg40Zn55Nd5 icosahedral quasicrystal phase and Mg7Zn3 columnar crystal matrix. In the growing process of Mg40Zn55Nd5 icosahedral quasicrystal phase, the growth morphology mainly depended on interface energy, adsorption effect of Nd and cooling rate.
关键词：