Synergistic Effect of Mo, W, Mn and Cr on the Passivation Behavior of a Fe-Based Amorphous Alloy Coating
来源期刊：Acta Metallurgica Sinica2018年第3期
论文作者：Wan-Ping Tian Hong-Wang Yang Suo-De Zhang
文章页码：308 - 320
摘 要：In this work, the electrochemical behaviors of SAM2 X5 Fe-based amorphous alloy coating and hard chromium coating were comparatively studied in 3.5 wt% Na Cl solution. In comparison with the hard chromium coating, the SAM2 X5 coating exhibited a wider and stable passive region with lower passive current density in the potentiodynamic polarization and showed a considerably lower current density at different anodic potentials in the potentiostatic polarization. In order to understand the passivation mechanism of the Fe-based amorphous coating, the components of the passive films formed at various polarization potentials were examined by X-ray photoelectron spectroscopy. The synergistic effect of Mo, W, Mn and Cr in the passive films was systemically analyzed. It has been revealed that Mo and W facilitate the formation of compact and stable Cr2O3 passive film at lower potentials, and the substantial enrichment of Mn in the passive film enhances the passivation ability at relatively higher potentials. The deep understanding of the passivation characteristics in multicomponent alloy systems could provide a guide for the design of corrosion-resistant amorphous alloy coatings for engineering applications.
Wan-Ping Tian1,2，Hong-Wang Yang1，Suo-De Zhang2
1. School of Materials Science and Engineering, Shenyang University of Technology2. Shenyang National Laboratory for Materials Science,Institute of Metal Research, Chinese Academy Sciences
摘 要：In this work, the electrochemical behaviors of SAM2 X5 Fe-based amorphous alloy coating and hard chromium coating were comparatively studied in 3.5 wt% Na Cl solution. In comparison with the hard chromium coating, the SAM2 X5 coating exhibited a wider and stable passive region with lower passive current density in the potentiodynamic polarization and showed a considerably lower current density at different anodic potentials in the potentiostatic polarization. In order to understand the passivation mechanism of the Fe-based amorphous coating, the components of the passive films formed at various polarization potentials were examined by X-ray photoelectron spectroscopy. The synergistic effect of Mo, W, Mn and Cr in the passive films was systemically analyzed. It has been revealed that Mo and W facilitate the formation of compact and stable Cr2O3 passive film at lower potentials, and the substantial enrichment of Mn in the passive film enhances the passivation ability at relatively higher potentials. The deep understanding of the passivation characteristics in multicomponent alloy systems could provide a guide for the design of corrosion-resistant amorphous alloy coatings for engineering applications.