Influence of heat treatment on tribological behaviors of novel wrought aluminum bronze
来源期刊：中国有色金属学报(英文版)2002年第4期
论文作者：张卫文 倪东惠 夏伟 邱诚 陈维平
文章页码：770 - 774
Key words：aluminum bronze; heat treatment; tribological behaviors
Abstract: Influence of heat treatment on mechanical properties and tribological behaviors of Ti and B modified wrought aluminum bronze were studied. The results show that different strength and plasticity combination of the alloy after solution treatment can be obtained by adjusting the ageing temperature. When aged at 450℃, the tensile strength σb, yield strength σ0.2, elongation δ and hardness of the alloy are 1050MPa, 780MPa, 4.5%, HB282, respectively. When aged at 650℃, those of the alloy are 905MPa, 600MPa, 12%, HB232, respectively. Under boundary lubrication condition with pressure above 22.2MPa, alloy with low temperature ageing has the best wear property. However, under the condition involving impact or shock loading, alloy with high temperature ageing is preferable. If the load is not heavy, the alloy under extrusion state is favorable for wear-resisting parts.