Designing multilayer diamond like carbon coatings for improved mechanical properties
来源期刊：JOURNAL OF MATERIALS SCIENCE TECHNOLOG2021年第6期
论文作者：Mohammad Sharear Kabir Zhifeng Zhou Zonghan Xie Paul Munroe
文章页码：108 - 117
摘 要：New multilayer coatings were produced by incorporating alternating soft and hard DLC layers enabled by varying the bias voltage during deposition process while maintaining a constant hard-to-soft layer thickness ratio. These coatings were deposited onto a Cr/Cr Cxgraded layer by closed field unbalanced magnetron sputtering（CFUBMS）. The cross-sectional analysis of the coatings showed that the multilayer coatings possess sharp interfaces between the soft and hard layers with the hard to soft layer thickness ratio（1:1.33） constant in all the coatings. Raman analysis uncovered the increasing sp3 character of the DLC coatings as a result of decreasing ID/IGratio and increasing full width at half maximum（FWHM）values of the G band peak induced supposedly by an increase in bias voltage during hard layer deposition.Nanoindentation tests showed an increase in hardness of the DLC coatings which can be correlated with the increase in the sp3 content of the coatings as well as decreasing sp2-C cluster size, as calculated from the ID/IGratio. Furthermore, the coatings exhibited excellent plastic deformation resistance and adhesion strength upon microindentation and scratch testing, respectively. Although further investigations are required to assess coating durability, the multilayer design could offer the DLC coatings with a rare opportunity to combine the high hardness with damage resistance with a constant bilayer thickness and without the need to introduce complex multilayer system.
Mohammad Sharear Kabir1,2，Zhifeng Zhou3，Zonghan Xie4,5，Paul Munroe1
1. School of Materials Science and Engineering, University of New South Wales2. mine Alloy, Institute for Frontier Materials, Deakin University3. Advanced Coatings Applied Research Laboratory, Department of Mechanical and Biomedical Engineering, City University of Hong Kong4. School of Mechanical Engineering, University of Adelaide5. School of Engineering, Edith Cowan University
摘 要：New multilayer coatings were produced by incorporating alternating soft and hard DLC layers enabled by varying the bias voltage during deposition process while maintaining a constant hard-to-soft layer thickness ratio. These coatings were deposited onto a Cr/Cr Cxgraded layer by closed field unbalanced magnetron sputtering（CFUBMS）. The cross-sectional analysis of the coatings showed that the multilayer coatings possess sharp interfaces between the soft and hard layers with the hard to soft layer thickness ratio（1:1.33） constant in all the coatings. Raman analysis uncovered the increasing sp3 character of the DLC coatings as a result of decreasing ID/IGratio and increasing full width at half maximum（FWHM）values of the G band peak induced supposedly by an increase in bias voltage during hard layer deposition.Nanoindentation tests showed an increase in hardness of the DLC coatings which can be correlated with the increase in the sp3 content of the coatings as well as decreasing sp2-C cluster size, as calculated from the ID/IGratio. Furthermore, the coatings exhibited excellent plastic deformation resistance and adhesion strength upon microindentation and scratch testing, respectively. Although further investigations are required to assess coating durability, the multilayer design could offer the DLC coatings with a rare opportunity to combine the high hardness with damage resistance with a constant bilayer thickness and without the need to introduce complex multilayer system.
关键词：