Plastic anisotropy calculation of severely-deformed Al-Mg-Si alloy considering texture changes in electron backscatter diffraction
来源期刊:JOURNAL OF MATERIALS SCIENCE TECHNOLOG2019年第7期
论文作者:I Putu Widiantara Hae Woong Yang Min Jun Kim Young Gun Ko
文章页码:1439 - 1443
摘 要:The investigation studied the plastic anisotropy of the severely-deformed Al-Mg-Si alloy by considering texture changes.The sample deformed via asymmetrical rolling under cross-shear condition was annealed at 598 K where recrystallization was in progress.It is found upon annealing that the intensity of Cube({001}100)was comparable to those of plane-strain components while the intensities of shear components remained constant despite their instabilities in the recrystallization regime.After annealing,the average Lankford value(■)of the present sample was close to a unity whereas the in-plane anisotropy(r)decreased,resulting in nearly isotropic characteristics of Al-Mg-Si alloy.
I Putu Widiantara,Hae Woong Yang,Min Jun Kim,Young Gun Ko
Plasticity Control & Mechanical Modeling Lab., School of Materials Science & Engineering, Yeungnam University
摘 要:The investigation studied the plastic anisotropy of the severely-deformed Al-Mg-Si alloy by considering texture changes.The sample deformed via asymmetrical rolling under cross-shear condition was annealed at 598 K where recrystallization was in progress.It is found upon annealing that the intensity of Cube({001}100)was comparable to those of plane-strain components while the intensities of shear components remained constant despite their instabilities in the recrystallization regime.After annealing,the average Lankford value(■)of the present sample was close to a unity whereas the in-plane anisotropy(r)decreased,resulting in nearly isotropic characteristics of Al-Mg-Si alloy.