Structure and electrochemical hydrogen storage characteristics of the as-cast and annealed La0.8-xSmxMg0.2Ni3.15Co0.2Al0.1Si0.05 （x=0-0.4） alloys
来源期刊：Journal of Rare Earths2012年第7期
论文作者：李平 候忠辉 杨泰 尚宏伟 曲选辉 张羊换
文章页码：696 - 704
摘 要：In order to ameliorate the electrochemical cycle stability of the RE-Mg-Ni based A2B7-type electrode alloys, the Mg content in the alloy was reduced and La in the alloy was partially substituted by Sm. The La0.8-xSmxMg0.2Ni3.15Co0.2Al0.1Si0.05 （x=0, 0.1, 0.2, 0.3, 0.4） elec-trode alloys were fabricated by casting and annealing. The microstructures of the as-cast and annealed alloys were characterized by XRD and SEM. The electrochemical hydrogen storage characteristics of the as-cast and annealed alloys were measured. The results revealed that all of the experimental alloys mainly consisted of two phases: （La,Mg）2Ni7 phase with the hexagonal Ce2Ni7-type structure and LaNi5 phase with the hexagonal CaCu5-type structure. As Sm content grew from 0 to 0.4, the discharge capacity and the high rate discharge ability （HRD） first in-creased and then decreased for the as-cast and annealed alloys, whereas the capacity retaining rate （S100） after 100 cycles increased continuously.
李平1，候忠辉2，杨泰2，尚宏伟2，曲选辉1，张羊换2
1. School of Materials Science and Engineering, University of Science and Technology Beijing2. Elected State Key Laboratory, Inner Mongolia University of Science and Technology
摘 要：In order to ameliorate the electrochemical cycle stability of the RE-Mg-Ni based A2B7-type electrode alloys, the Mg content in the alloy was reduced and La in the alloy was partially substituted by Sm. The La0.8-xSmxMg0.2Ni3.15Co0.2Al0.1Si0.05 （x=0, 0.1, 0.2, 0.3, 0.4） elec-trode alloys were fabricated by casting and annealing. The microstructures of the as-cast and annealed alloys were characterized by XRD and SEM. The electrochemical hydrogen storage characteristics of the as-cast and annealed alloys were measured. The results revealed that all of the experimental alloys mainly consisted of two phases: （La,Mg）2Ni7 phase with the hexagonal Ce2Ni7-type structure and LaNi5 phase with the hexagonal CaCu5-type structure. As Sm content grew from 0 to 0.4, the discharge capacity and the high rate discharge ability （HRD） first in-creased and then decreased for the as-cast and annealed alloys, whereas the capacity retaining rate （S100） after 100 cycles increased continuously.
关键词：