Influence of Bi Addition on Pure Sn Solder Joints: Interfacial Reaction, Growth Behavior and Thermal Behavior
来源期刊：Journal Of Wuhan University Of Technology Materials Science Edition2019年第3期
论文作者：赖彦青 胡小武 LI Yulong JIANG Xiongxin
文章页码：668 - 675
摘 要：The effects of different Bi contents on the properties of Sn solders were studied. The interfacial reaction and growth behavior of intermetallic compounds（IMCs） layer（η-Cu6 Sn5 + e-Cu3 Sn） for various soldering time and the influence of Bi addition on the thermal behavior of Sn-x Bi solder alloys were investigated. The Cu6 Sn5 IMC could be observed as long as the molten solder contacted with the Cu substrate. However, with the longer welding time such as 60 and 300 s, the Cu3 Sn IMC was formed at the interface between Cu6 Sn5 and Cu substrate. With the increase of soldering time, the thickness of total IMCs increased, meanwhile, the grain size of Cu6 Sn5 also increased. An appropriate amount of Bi element was beneficial for the growth of total IMCs,but excessive Bi（≥ 5 wt%） inhibited the growth of Cu6 Sn5 and Cu3 Sn IMC in Sn-x Bi/Cu microelectronic interconnects. Furthermore, with the Bi contents increasing（Sn-10 Bi solder in this present investigation）, some Bi particles accumulated at the interface between Cu6 Sn5 layer and the solder.
赖彦青，胡小武，LI Yulong，JIANG Xiongxin
摘 要：The effects of different Bi contents on the properties of Sn solders were studied. The interfacial reaction and growth behavior of intermetallic compounds（IMCs） layer（η-Cu6 Sn5 + e-Cu3 Sn） for various soldering time and the influence of Bi addition on the thermal behavior of Sn-x Bi solder alloys were investigated. The Cu6 Sn5 IMC could be observed as long as the molten solder contacted with the Cu substrate. However, with the longer welding time such as 60 and 300 s, the Cu3 Sn IMC was formed at the interface between Cu6 Sn5 and Cu substrate. With the increase of soldering time, the thickness of total IMCs increased, meanwhile, the grain size of Cu6 Sn5 also increased. An appropriate amount of Bi element was beneficial for the growth of total IMCs,but excessive Bi（≥ 5 wt%） inhibited the growth of Cu6 Sn5 and Cu3 Sn IMC in Sn-x Bi/Cu microelectronic interconnects. Furthermore, with the Bi contents increasing（Sn-10 Bi solder in this present investigation）, some Bi particles accumulated at the interface between Cu6 Sn5 layer and the solder.
关键词：