Forming regularity and relation between composition and property of B2O3-BaO-ZnO glass①
来源期刊：中南大学学报(英文版)2005年第5期
论文作者：卢安贤 李雪 林娜
文章页码：521 - 525
Key words：B2O3-BaO-ZnO glass; glass forming range; thermal expansion coefficient; transition temperature;resistivity
Abstract: B2O3-BaO-ZnO glass was prepared by using conventional melt quenching technology. The forming regularity and the relationship between the composition and the property of B2O3BaO ZnO glass were investigated.The results show that the composition range for forming B2O3BaO ZnO glass is very wide, but the content of B2O3 has a limit within mole fraction of 25% 75%. When the content of B2O3 is over the limit, the melt will be divided into two phases with different compositions and structures, whereas too low content of B2O3 will result in the crystallization of the melt during the cooling process. The thermal expansion coefficient, the transition temperature and the resistivity of the glass at room temperature are (5 10)×10-6℃-1, 480 620℃and (1.5 3.0)×1010Ω·m,respectively.