Influences of Yttrium on Adhesion of Oxide Scale of Fe-Cr-Al Alloy
来源期刊：JOURNAL OF RARE EARTHS2001年第2期
论文作者：王福会 李美栓 辛丽 李铁藩 周龙江
Abstract: The 1100 ℃ isothermal oxidation behavior of Fe-23Cr-5Al alloy modified by yttrium addition was studied by means of thermogravimetric analysis, scanning electron microscopy and energy dispersive X-ray analysis. Yttrium was added to this alloy in the forms of metallic addition, yttrium oxide and ion implant. Cracking and spalling occurred on the convoluted scale formed on Y-free alloy and exposed the substrate. A flat dense scale without spallation was formed on the yttrium alloying addition or yttrium oxide dispersion alloy. The scale adhesion was also improved by 1×1017Y＋／cm2-implantation. The results indicate the convoluted morphology of the scale on Fe-23Cr-5Al-0.21Ti alloy is related to the growth mechanism of the alumina scale, and the spallation of the scale is related to sulfur segregation at the scale/alloy interface. The main reason that the adhesion of alumina scale is improved by yttrium addition lies in the following. Yttrium is liable to form a stable yttrium sulfide with sulfur in the alloy and prevent sulfur interface from segregation. Another reason is that the growth mechanism of alumina scale is changed by yttrium addition.
王福会1，李美栓1，辛丽1，李铁藩1，周龙江1
(1.Corrosion Science Laboratory, Institute of Corrosion and Protection of Metals, Chinese Academy of Sciences,)
Abstract:The 1100 ℃ isothermal oxidation behavior of Fe-23Cr-5Al alloy modified by yttrium addition was studied by means of thermogravimetric analysis, scanning electron microscopy and energy dispersive X-ray analysis. Yttrium was added to this alloy in the forms of metallic addition, yttrium oxide and ion implant. Cracking and spalling occurred on the convoluted scale formed on Y-free alloy and exposed the substrate. A flat dense scale without spallation was formed on the yttrium alloying addition or yttrium oxide dispersion alloy. The scale adhesion was also improved by 1×1017Y＋／cm2-implantation. The results indicate the convoluted morphology of the scale on Fe-23Cr-5Al-0.21Ti alloy is related to the growth mechanism of the alumina scale, and the spallation of the scale is related to sulfur segregation at the scale/alloy interface. The main reason that the adhesion of alumina scale is improved by yttrium addition lies in the following. Yttrium is liable to form a stable yttrium sulfide with sulfur in the alloy and prevent sulfur interface from segregation. Another reason is that the growth mechanism of alumina scale is changed by yttrium addition.
【全文内容正在添加中】